Carbon-supported Pt-Co catalysts prepared by a modifled polyol process as cathodes for PEM fuel cells

In this work, carbon-supported Pt70Co30 nanoparticles were prepared by a polyol process using a long-chain diol as reducer (hexadecanediol) and oleic acid and oleylamine as stabilizers. Depending on the synthesis conditions, Pt70Co30/C nanocatalysts with very small particle size (1.9 +/- 0.2 nm) and narrow distribution homogeneously dispersed on the carbon support and having a high degree of alloying without the need of thermal treatments were obtained. The as-prepared catalyst presents an excellent performance as proton exchange membrane fuel cells (PEMFC) cathode material. In terms of mass activity (MA), the Pt70Co30/C electrocatalysts produced single fuel cell polarization response superior to that of commercial catalyst. To analyze alloying effects, the result of thermal treatment at low temperatures (200-400 degrees C) was also evaluated and an increase of average crystallite size and a lower degree of alloying, probably associated to cobalt oxidation, were evidenced

Influence of particle size on the properties of Pt-Ru/C catalysts prepared by a microemulsion method

Pt-Ru/C nanocatalysts were prepared by a microemulsion method using different values of water/surfactant molar ratio in order to get different particle sizes. Crystallite sizes and structural properties were determined by X-ray diffraction. Particle size and distribution were characterized by transmission electron microscopy and average composition was determined by energy-dispersive X-ray analysis. Thermogravimetric analysis was used to estimate the amount of supported metals. Differential scanning calorimetry measurements indicated the presence of hydrous ruthenium oxides in the as-prepared catalysts. Results for the oxidation of adsorbed CO as well as for methanol oxidation revealed significant differences in the behavior of the prepared catalysts. All together, the results demonstrate that the variation of particle size produces changes in other properties of the Pt-Ru/C catalysts and that to establish direct correlations between electrocatalytic activity and particle size is not possible because the effects of the different parameters cannot be separated. (c) 2007 the Electrochemical Society

The Aerosol OT + n-butanol + n-heptane + water system: Phase behavior, structure characterization, and application to Pt70Fe30 nanoparticle Synthesis

A phase diagram of the pseudo-ternary Aerosol OT (AOT) + n-butanol/n-heptane/water system, at a mass ratio of AOT/n-butanol = 2, is presented. Conductivity measurements showed that within the vast one-phase microemulsion region observed, the structural transition from water-in-oil to oil-in-water microemulsion occurs continuously without phase separation. This pseudo-ternary system was applied to the synthesis of carbon-supported Pt 70Fe30 nanoparticles, and it was found that nanoparticles prepared in microemulsions containing n-butanol have more Fe than those prepared in ternary microemulsions of AOT/n-heptane/water under similar conditions. It was verified that introducing n-butanol as a cosurfactant into the AOT/n-heptane/water system lead to complete reduction of the Fe ions that allowed obtaining alloyed PtFe nanoparticles with the desired composition, without the need of preparing functionalized surfactants and/or the use of inert atmosphere. © 2007 American Chemical Society