    Properties of lanthanum doped BaTiO3 produced from nanopowders

    Get PDF
    Pure and barium titanate (BT) powders doped with different lanthanum concentration were prepared by the polymeric precursor method (Pechini process) which was carried out as a three-stage process from organometallic complexes. Sintering of pressed powders was performed at 1300 8C for 2, 4 and 8 h. XRD analysis showed cubic BT powders with crystallite sizes between 20 and 25 nm and tetragonal crystal structure of BT ceramics. The influence of sintering time on grain growth was fairly obvious. It was found that lanthanum doping has significant effect on powders particle size and ceramics grain size. The influence of lanthanum concentration on grain size inhibition, improving the dielectric properties of BT ceramics was detected. The relation between sintering time, grain size, structure and electrical properties of the BT ceramics was analyzed

    Interaction of Gold Nanoparticles in Barium Titanate Thin Films

    Full text link
    A novel approach to control the grain size of oxide thin film materials has been investigated. Perovskite BaTiO3 shows interesting grain structures when deposited on gold predeposited, (111)-oriented, singlecrystal SrTiO3 substrates. Solid oxide films grow epitaxially on patterned seed layers and show variations in grain size relative to the films deposited on SrTiO3 directly.Comment: 14 pages, 4 figure

    Screen printed PLZT thick films prepared from nanopowders

    No full text
    The gap between the bulk materials and thin films can be filled with thick films suitably designed and appropriate processed. Thick films of complex system like lead-lanthanum-zirconium titanate (PLZT) is difficult to produce by simple solid-state reaction keeping compositional homogeneity and optimal grain size distribution. In the present work, PLZT thick films were fabricated by screen-printing technique from nanosized powders obtained through soft chemistry by polymeric precursor method. Thick film paste was obtained by mixing PLZT fine powders and organic vehicle. The upper and bottom electrodes based on Ag-Pd and functional component based on PLZT were screen-printed on alumina substrate and after that annealed in air atmosphere. The powder morphology, microstructure, dielectric and ferroelectric properties of 9.5/65/35 PLZT thick films were analysed. (c) 2007 Elsevier Ltd. All rights reserved

    Structure and Properties of Barium Bismuth Titanate Prepared by Mechanochemical Synthesis

    No full text
    Bi4Ti4O15 [BBT], a member of Aurivillius bismuth-based layer-structure perovskites, was prepared from stoichiometric amounts of BaTiO3 [BT] and Bi4Ti3O12 [BIT] obtained via mechanochemical synthesis. Mechanochemical synthesis was performed in air atmosphere in a planetary ball mill. BBT ceramics were sintered at 1100C for 4 h without pre-calcination step within heating rate 10C/min. The formation of phase and crystal structure of BT, BIT and BBT were approved using X-ray analysis. The morphology of obtained powders and microstructure were exhamined using scanning electron microscopy. The electrical properties of sintered samples were carried out

    Lead-free BaBi4Ti4O15 ceramics: Effect of synthesis methods on phase formation and electrical properties

    No full text
    The processing of ferroelectric BaBi4Ti4O15 (BBT) ceramics from powders prepared by conventional solid state reaction (SSR) and mechanochemical activation (MA) has been investigated. It was shown that MA synthesis reduces the synthesis temperature of BBT powders, leading to smaller particles with reduced anisotropy and consequently to smaller grain size of ceramics. Dielectric properties were investigated in a wide range of temperatures (20-800 degrees C) and frequencies (1.21 kHz to 1 MHz). The relative dielectric permittivity at Curie temperature was higher for solid state obtained ceramics than for the mechanically treated ones. The conductivity of sintered samples was studied, suggesting decreasing of conductivity of BBT-MA in comparison with BBT-SS ceramics. The influence of the grain and the grain boundaries contribution to the dielectric behavior in both ceramics was analyzed through impedance spectroscopy. A well-defined ferroelectric hysteresis loop was obtained for both samples. (C) 2014 Elsevier Ltd and Techna Group S.r.l. All rights reserved

    Structure and properties of chemically synthesized BiFeO3. Influence of fuel and complexing agent

    No full text
    Perovskite, single multiferroic bismuth ferrite was prepared by two chemical methods: auto-combustion and soft chemical route. Influence of different fuels and complexing agents and thermal treatment on purity of bismuth ferrite powders and density of bismuth ferrite ceramics were investigated. X-ray diffraction technique (XRD) indicated that optimal temperatures and times for calcination and sintering are 600 degrees C for 2 h and 800 degrees C for 1 h with quenching, respectively. Scanning electron microscopy (SEM) analysis showed that soft route synthesized samples formed softer agglomerates and smaller grains with less secondary phases. Powders and pellets were characterized by Brunauer Emmett Teller (BET) specific surface area analysis, particle size distribution, Fourier transform infrared spectroscopy (FT-IR), dilatometry, Raman spectroscopy, X-ray photoelectron spectroscopy (XPS), dielectric and magnetic measurements. Resistivity and origin of electrical resistance were studied by means of impedance measurements. (C) 2014 Elsevier Ltd and Techna Group S.r.l. All rights reserved

    The electrical properties of chemically obtained barium titanate improved by attrition milling

    No full text
    Barium titanate ceramics were prepared using the nanopowder resulting from a polymeric precursor method, a type of modified Pechini process. The obtained nanopowder was observed to agglomerate and in order to de-agglomerate the powder and enhance the properties of the barium titanate the material was attrition milled. The impact of this attrition milling on the electrical properties of the barium titanate was analysed. The temperature dependence of the relative dielectric permittivity showed three structural phase transitions that are characteristic for ferroelectric barium titanate ceramics. The relative dielectric permittivity at the Curie temperature was higher for the attrition-treated sample than for the non-treated barium titanate. The dielectric losses were below 0.04 in both barium titanate ceramics. The grain and grain-boundary contributions to the total resistivity were observed using impedance analyses for both ceramics. A well-defined ferroelectric hysteresis loop and piezoelectric coefficient d(33) = 150 pC/N were obtained for the ceramics prepared from the de-agglomerated powder. In this way we were able to demonstrate that by attrition milling of chemically obtained powders the ferroelectric and piezoelectric properties of the ceramics could be enhanced