Laser weld: microstructure and corrosion study of Ag-Pd-Au-Cu alloy of the dental application

The laser Welding process was introduced into dentistry by the end of the 1980s, resulting on a great impulse to that area with the development of cheaper and smaller equipment, using simpler technique. This allowed greater use of that process on the confection of prostheses compared to the brazing process since the heat source for that process is a concentrated light beam of high power, which minimizes distortion problems on the prosthetic pieces. Ag-Pd-Au-Cu alloy used on the confection of dental implant prostheses was observed before and after subjection to the laser welding process. The microstructure was analyzed with the. use of optic microscopy and the corrosion resistance was studied by the traditional electrochemical techniques and by electrochemical impedance, under environmental conditions simulating the aggressiveness found in the mouth cavity. A structural change was detected on the weld area, which presented a refined microstructure deriving from the high-speed cooling. The base metal out of the weld area presented a fusion coarse microstructure. The electrochemical essays showed differences on the potentiodynamic polarization behavior in both weld and metal base areas, indicating superior corrosion resistance in the weld area. The impedance spectra were characterized by capacitive distorted components, presenting linear impedance in the low frequencies area. (C) 2002 Elsevier B.V. B.V. All rights reserved

Comparison of crystallinity between natural hydroxyapatite and synthetic cp-Ti /HA coatings

Commercial purity titanium (cp-Ti), and some of its alloys are important materials in the medical field because of their excellent biocompatibility and mechanical properties. Recently a simple chemical method to induce bioactivity in these inert metallic materials was reported. In this work, the biomimetic chemical process has been used to modify the surface of cp-Ti with the formation of a deposit layer of apatite (a calcium phosphate compound). The main purpose was to study the influence of heat treatment on changes in crystallinity in the deposited phases. X-ray diffraction analysis and scanning electron microscopy showed that the apatite coatings heat treated between 400 and 600 °C were less crystalline, similar to biological apatites. Upon heat treatment at temperatures above 700 °C, the apatite coatings appeared more crystalline, and were a mixture of hydroxyapatite, octacalcium phosphate and magnesium phosphate