5 research outputs found
Iridium-decorated multiwall carbon nanotubes and its catalytic activity with Shell 405 in hydrazine decomposition
Iridium-functionalized multiwalled carbon nanotubes (Ir-MWNT) are the future catalyst support material for hydrazine fuel decomposition. The present work demonstrates decoration of iridium particle on iron-encapsulated multiwalled carbon nanotubes (MWNT) by wet impregnation method in the absence of any stabilizer. Electron microscopy studies reveal the coated iridium particle size in the range of 5-10 nm. Elemental analysis by energy dispersive X-ray diffraction confirms 21 wt% of Ir coated over MWNT. X-ray photoelectron spectroscopy (XPS) shows 4f(5/2) and 4f(7/2) lines of iridium and confirms the metallic nature. The catalytic activity of Ir-MWNT/Shell 405 combination is performed in 1 N hydrazine micro-thrusters. The thruster performance shows increase in chamber pressure and decrease in chamber temperature when compared to Shell 405 alone. This enhanced performance is due to high thermal conducting nature of MWNTs and the presence of Ir active sites over MWNTs
Low temperature magnetoresistance and magnetization studies of iron encapsulated multiwall carbon nanotube/polyvinyl chloride composites
We present the experimental results of temperature dependent magnetoresistance (MR) and the magnetization studies of iron encapsulated multiwall carbon nanotube (MWCNT)/polyvinyl chloride (PVC) composites with different wt% of MWCNTs. Transmission electron microscopy characterization shows that MWCNTs are encapsulated with rod-shaped iron nanoparticles of aspect ratio of similar to 3. The MR behavior of 1.9 wt% MWCNT/PVC sample shows dominance of forward scattering and wave function shrinkage whereas, weak localization and electron-electron interactions explain the MR data of higher wt% samples (9.1, 16.6 and 44.4 wt%). The composites of 4.7 and 9.1 wt% exhibit ferromagnetic behavior at all temperatures with room temperature coercivities of similar to 1036 and 628 Oe, respectively. (C) 2014 Elsevier Ltd. All rights reserved
Characterization, charge transport and magnetic properties of multi-walled carbon nanotube-polyvinyl chloride nanocomposites
Multi-walled carbon nanotube (MWCNT)-polyvinyl chloride (PVC) nanocomposites, with MWCNT loading up to 44.4 weight percent (wt%), were prepared by the solvent mixing and casting method. Electron microscopy indicates high degree of dispersion of MWCNT in PVC matrix, achieved by ultrasonication without using any surfactants. Thermogravimetric analysis showed a significant monotonic enhancement in the thermal stability of nanocomposites by increasing the wt% of MWCNT. Electrical conductivity of nanocomposites followed the classical percolation theory and the conductivity prominently improved from 10(-7) to 9 S/cm as the MWCNT loading increased from 0.1 to 44.4 wt%. Low value of electrical percolation threshold similar to 0.2 wt% is achieved which is attributed to high aspect ratio and homogeneous dispersion of MWCNT in PVC. The analysis of the low temperature electrical resistivity data shows that sample of 1.9 wt% follows three dimensional variable range hopping model whereas higher wt% nanocomposite samples follow power law behavior. The magnetization versus applied field data for both bulk MWCNTs and nanocomposite of 44.4 wt% display ferromagnetic behavior with enhanced coercivities of 1.82 and 1.27 kOe at 10 K, respectively. The enhancement in coercivity is due to strong dipolar interaction and shape anisotropy of rod-shaped iron nanoparticles. (C) 2013 Elsevier B.V. All rights reserved