Impact of Sm³⁺ and Er³⁺ Cations on the Structural, Optical, and Magnetic Traits of Spinel Cobalt Ferrite Nanoparticles: Comparison Investigation

In this study, we investigated a comparison of the structure, morphology, optic, and magnetic (room temperature (RT)) features of Er3+ and Sm3+ codoped CoFe2O4 (CoErSm) nanospinel ferrite (NSFs) (x ≤ 0.05) synthesized via hydrothermal (H-CoErSm NSFs) and sonochemical (S-CoErSm NSFs) approaches. The formation of all products via both synthesis methods has been validated by X-ray powder diffraction (XRD) and scanning electron microscopy (SEM), along with energy-dispersive X-ray (EDX) and transmission electron microscopy (TEM) techniques. The single phase of the spinel structure (except for the Hyd sample with x = 0.03) was evidenced by XRD analysis. The DXRD (crystallite size) values of H-CoErSm and S-CoErSm NSFs are in the 10-14.7 and 10-16 nm ranges, respectively. TEM analysis presented the cubic morphology of all products. A UV-visible percent diffuse reflectance (DR %) study was performed on all products, and Eg (direct optical energy band gap) values varying in the 1.32-1.48 eV range were projected from the Tauc plots. The data of RT magnetization demonstrated that all prepared samples are ferromagnetic in nature. M-H data revealed that rising the contents of cosubstituent elements (Sm3+ and Er3+ ions) caused an increase in Ms (saturation magnetization) and Hc (coercive field) in comparison to pristine samples. Although concentration dependence is significant (x > 0.02), no strict regularity (roughly fluctuating) has been ruled out in Ms values for doped samples prepared via the hydrothermal method. However, sonochemically prepared samples demonstrated that Ms values increase with increasing x up to x = 0.04 and then decrease with the further rise in cosubstituent Sm3+ and Er3+ ions. The calculated values of Ms and Hc were found to be greater in H-CoErSm NSFs compared to those in S-CoErSm NSFs. The present investigation established that the distribution of cations and the variation in crystallite/particle sizes are efficient to control the intrinsic properties of all samples

Impact of Tm³⁺ and Tb³⁺ rare earth cations substitution on the structure and magnetic parameters of Co-Ni nanospinel ferrite

Tm-Tb co-substituted Co-Ni nanospinel ferrites (NSFs) as (Co0.5Ni0.5) [TmxTbxFe2−2x]O4 (x = 0.00–0.05) NSFs were attained via the ultrasound irradiation technique. The phase identification and morphologies of the NSFs were explored using X-rays diffraction (XRD), selected area electron diffraction (SAED), and transmission and scanning electronic microscopes (TEM and SEM). The magnetization measurements against the applied magnetic field (M-H) were made at 300 and 10 K with a vibrating sample magnetometer (VSM). The various prepared nanoparticles revealed a ferrimagnetic character at both 300 and 10 K. The saturation magnetization (Ms), the remanence (Mr), and magneton number (nB) were found to decrease upon the Tb-Tm substitution effect. On the other hand, the coercivity (Hc) was found to diminish with increasing x up to 0.03 and then begins to increase with further rising Tb-Tm content. The Hc values are in the range of 346.7–441.7 Oe at 300 K to 4044.4–5378.7 Oe at 10 K. The variations in magnetic parameters were described based on redistribution of cations, crystallites and/or grains size, canting effects, surface spins effects, super-exchange interaction strength, etc. The observed magnetic results indicated that the synthesized (Co0.5Ni0.5)[TmxTbxFe2−x]O4 NSFs could be considered as promising candidates to be used for room temperature magnetic applications and magnetic recording media