379 research outputs found
Superconductivity in metal rich Li-Pd-B ternary Boride
8K superconductivity was observed in the metal rich Li-Pd-B ternary system.
Structural, microstructural, electrical and magnetic investigations for various
compositions proved that Li2Pd3B compound, which has a cubic structure composed
of distorted Pd6B octahedrons, is responsible for the superconductivity. This
is the first observation of superconductivity in metal rich ternary borides
containing alkaline metal and Pd as a late transition metal. The compound
prepared by arc melting has high density, is stable in the air and has an upper
critical field, Hc2(0), of 6T.Comment: 4 pages, 5 figur
Niobium based intermetallics as a source of high-current/high-magnetic field superconductors
The article is focused on low temperature intermetallic A15 superconducting
wires development for Nuclear Magnetic Resonance, NMR, and Nuclear Magnetic
Imaging, MRI, magnets and also on cryogen-free magnets. There are many other
applications which would benefit from new development such as future Large
Hadron Collider to be built from A15 intermetallic conductors. This paper
highlights the current status of development of the niobium based
intermetallics with special attention to Nb 3 (Al 1-x, Ge x). Discussion is
focused on the materials science aspects of conductor manufacture, such as
b-phase (A15) formation, with particular emphasis on the maximisation of the
superconducting parameters, such as critical current density, Jc, critical
temperature, Tc, and upper critical field, Hc2 . Many successful manufacturing
techniques of the potential niobium-aluminide intermetallic superconducting
conductors, such as solid-state processing, liquid-solid processing, rapid
heating/cooling processes, are described, compared and assessed. Special
emphasis has been laid on conditions under which the Jc (B) peak effect occurs
in some of the Nb3(Al,Ge) wires. A novel electrodeoxidizing method developed in
Cambridge whereby the alloys and intermetallics are produced cheaply making all
superconducting electromagnetic devices, using low cost LTCs, more cost
effective is presented.This new technique has potential to revolutionise the
existing superconducting industry enabling reduction of cost orders of
magnitude.Comment: Paper presented at EUCAS'01 conference, Copenhagen, 26-30 August 200
Superconducting Properties of MgB2 Bulk Materials Prepared by High Pressure Sintering
High-density bulk materials of a newly discovered 40K intermetallic MgB2
superconductor were prepared by high pressure sintering. Superconducting
transition with the onset temperature of 39K was confirmed by both magnetic and
resistive measurements. Magnetization versus field (M-H) curve shows the
behavior of a typical Type II superconductor and the lower critical field
Hc1(0) estimated from M-H curve is 0.032T. The bulk sample shows good
connection between grains and critical current density Jc estimated from the
magnetization hysteresis using sample size was 2x104A/cm2 at 20K and 1T. Upper
critical field Hc2(0) determined by extrapolating the onset of resistive
transition and assuming a dirty limit is 18T.Comment: 3Pages PD
Magnetization measurements on Li2Pd3B superconductor
Magnetization in DC magnetic fields and at different temperatures have been
measured on the Li2Pd3B compound. This material was recently found to show
superconductivity at 7-8K. Critical fields Hc1(0) and Hc2(0) have been
determined to be 135Oe and 4T, respectively. Critical current density, scaling
of the pinning force within the Kramer model and the irreversibility field data
are presented. Several superconductivity parameters were deduced: x(csi)=9.1
nm, l(lamda)=194nm and k=21. The material resembles other boride
superconductors from the investigated points of view.Comment: 10 pages, 5 figure
A Cross-Whiskers Junction as a Novel Fabrication Process for Intrinsic Josephson Junction
A Bi2Sr2CaCu2O8+d cross-whiskers junction has been successfully discovered as
a novel intrinsic Josephson junction without using any technique for
micro-fabrication. Two Bi2Sr2CaCu2O8+d whisker crystals were placed crosswise
on a MgO substrate and heated at 850C for 30 min. They were electrically
connected at their c-planes. The measurement terminals were made at the four
ends of the whiskers. The I-V characteristics of the cross-whiskers junction at
5K were found to show a clear multiple-branch structure with a spacing of
approximately 15 mV that is a feature of the intrinsic Josephson junction. The
critical current density Jc was estimated to be 1170 A/cm2. The
branch-structure was strongly suppressed by the magnetic field above 1kOe.Comment: 4 pages, PDF fil
One-neutron knockout reaction of 17C on a hydrogen target at 70 MeV/nucleon
First experimental evidence of the population of the first 2- state in 16C
above the neutron threshold is obtained by neutron knockout from 17C on a
hydrogen target. The invariant mass method combined with in-beam gamma-ray
detection is used to locate the state at 5.45(1) MeV. Comparison of its
populating cross section and parallel momentum distribution with a Glauber
model calculation utilizing the shell-model spectroscopic factor confirms the
core-neutron removal nature of this state. Additionally, a previously known
unbound state at 6.11 MeV and a new state at 6.28(2) MeV are observed. The
position of the first 2- state, which belongs to a member of the lowest-lying
p-sd cross shell transition, is reasonably well described by the shell-model
calculation using the WBT interaction.Comment: 15 pages, 3 figure
Search for low lying dipole strength in the neutron rich nucleus Ne
Coulomb excitation of the exotic neutron-rich nucleus Ne on a
Pb target was measured at 58 A.MeV in order to search for low-lying E1
strength above the neutron emission threshold. Data were also taken on an
Al target to estimate the nuclear contribution. The radioactive beam
was produced by fragmentation of a 95 A.MeV Ar beam delivered by the
RIKEN Research Facility. The set-up included a NaI gamma-ray array, a charged
fragment hodoscope and a neutron wall. Using the invariant mass method in the
Ne+n channel, we observe a sizable amount of E1 strength between 6 and
10 MeV. The reconstructed Ne angular distribution confirms its E1
nature. A reduced dipole transition probability of B(E1)=0.490.16
is deduced. For the first time, the decay pattern of low-lying
strength in a neutron-rich nucleus is obtained. The results are discussed in
terms of a pygmy resonance centered around 9 MeV
Low-Energy Charge-Density Excitations in MgB: Striking Interplay between Single-Particle and Collective Behavior for Large Momenta
A sharp feature in the charge-density excitation spectra of single-crystal
MgB, displaying a remarkable cosine-like, periodic energy dispersion with
momentum transfer () along the -axis, has been observed for the first
time by high-resolution non-resonant inelastic x-ray scattering (NIXS).
Time-dependent density-functional theory calculations show that the physics
underlying the NIXS data is strong coupling between single-particle and
collective degrees of freedom, mediated by large crystal local-field effects.
As a result, the small- collective mode residing in the single-particle
excitation gap of the B bands reappears periodically in higher Brillouin
zones. The NIXS data thus embody a novel signature of the layered electronic
structure of MgB.Comment: 5 pages, 4 figures, submitted to PR
- …