Nitrogen doping into titanium dioxide by the sol–gel method using nitric acid

N-doped TiO(2) has been prepared by use of sol-gel systems containing titanium alkoxide, with nitric acid as the nitrogen source. The time needed for gelation of the systems was drastically reduced by ultrasonic irradiation. The peaks assigned to the nitrate and nitrous ions were observed by FT-IR measurement during the sol-gel reaction. The N-doping was confirmed by the observation of N-O peaks in the XPS spectrum of the sample heated at 400 A degrees C. The nitrate ion acted as an oxidizer of the ethanol solvent and titanium species. The TiO(2) became doped with nitrogen oxide species as a result of reduction of nitrate ion incorporated into the dried gel samples. These results indicated that the added nitric acid was reduced during the sol-gel transition and heating process, and the resulting NO species were situated in the titania networks. The UV and visible photocatalytic activity of the samples was confirmed by the degradation of trichloroethylene.ArticleRESEARCH ON CHEMICAL INTERMEDIATES. 37(8):869-881 (2011)journal articl

Ion beam sputtering deposition of silver nanoparticles and TiOx/ZnO nanocomposites for use in surface enhanced vibrational spectroscopy (SERS and SEIRAS)

Hybrids consisting of silver nanoparticles (in varying fractions) and of TiOx/ZnO were prepared via top-down ion beam sputtering (IBS) deposition on silicon substrates. The deposited nanomaterials were characterized by scanning electron microscopy and X-ray photoelectron spectroscopy. It is shown that such composites represent a viable substrate for use in both surface enhanced Raman spectroscopy (SERS) and surface enhanced infrared absorption spectroscopy (SEIRAS), as exemplarily shown for crystal violet as the model analyte. The C-H bending mode at about 1181 cmâ1and the C-N vibration at 1361 cmâ1observed in the SERS and SEIRAS spectra, respectively, have been used as analytical signal. The substrate consisting of TiOx NPs with 33% fraction of silver provides the strongest enhancement in SERS (up to 10,000-fold), while TiOx/AgNPs with thickness of 2 and 1 nm in ion beam sputtering, respectively, provides the best sensitivity in SEIRAS. The substrates also display photocatalytic activity as shown by the degradation of adsorbed crystal violet under ultraviolet irradiation