Effect of alloy treatment and coiling temperature on microstructure and bending performance of ultra-high strength strip steel

Two different high strength B-containing microalloyed steel strips produced in industrial processing conditions, one treated with Ti and the other treated with Al, processed by controlled rolling, accelerated cooling and coiling in two different temperatures ranges [723 K to 733 K (450 °C to 460 °C)] and [633 K to 653 K (360 °C to 380 °C)] were subjected to bend testing. The Ti treated steel coiled at the higher temperature 733 K (460 °C) showed the best bending performance. The relatively softer (tensile strength of and even {112} in the sub-surface region as well as uniformity of through thickness texture of the rolled sheet improve the bendability. In the presence of crack initiators, like coarse and brittle TiN particles found in the Ti treated steel, a harder microstructure and the presence of Cube and Goss texture in the sub-surface layer, seen for the lower coiling temperature can cause local transgranular cleavage cracking. Finally the post-uniform elongation obtained from tensile testing and bendability follow a good correlation

The phytobenthos of the Hornsund fiord, SW Spitsbergen

The species composition and biomass of material collected in the summers 1981 and 1983 from 69 stations in the Hornsund fiord were analysed. 48 macroalgal taxa were found: 13 green algae, 18 brown algae and 17 red algae. 19 of these taxa were not reported from the nearby Isfjorden. The overall biomass for the littoral zone varied from 0 to 216gnT2 formalin d.w., although in J of samples the biomass was between 20 and 80 gm_z. The dominant species were Fucus distichus, Acrosiphonia duriusada and Pilayella littoralis. Using cluster analysis, an attempt was made to delimit regions with a characteristic species composition. The results obtained, however, do not permit this in the littoral zone of the Hornsund fiord