Synthesis of the semi-organic nonlinear optical crystal l-glutamic acid zinc chloride and investigation of its growth and physiochemical properties

The aim of this study is to synthesize and investigate the growth and physiochemical properties of the nonlinear optical semi-organic crystal l-glutamic acid zinc chloride (LGAZC). An optically transparent and defect-free crystal was grown with the slow evaporation solution growth technique under optimized conditions. The induction periods were measured at various supersaturations, and the interfacial energies were evaluated. Single crystal X-ray diffraction reveals that the crystal has an orthorhombic structure with space group P212121, and the calculated lattice parameters are a = 5.20 Ã, b = 6.99 Ã, c = 17.58 Ã, α = β = γ = 90° and volume = 623.411 Ã3. Spectroscopic properties were investigated by recording the Fourier transform infrared and optical transmission spectra. The thermal decomposition of the grown crystal was investigated by Thermo Gravimetric and Differential Thermal Analysis (TG/DTA). The LGAZC crystal exhibits second harmonic generation (SHG) efficiency 1.5 times that of inorganic KDP crystal. The presence of the metal ion (Zn+) in a grown crystal was identified by EDAX spectrum analysis. The photoconductivity study demonstrates that LGAZC crystal has a positive photo conducting nature. The dielectric response of the LGAZC crystal was investigated and reported. Keywords: Semi-organic nonlinear optical crystal, X-ray Diffraction, UV-vis-NIR, Thermal stud

Synthesis, growth and characterization of semiorganic nonlinear optical single crystal bis(thiourea) barium nitrate (BTBN) for frequency conversion

A novel semiorganic nonlinear optical (NLO) crystal, bis(thiourea) barium nitrate (BTBN) was synthesized and grown by slow evaporation method. Structure of the new crystalline compound was confirmed by single crystal X-ray diffraction analysis and it showed that BTBN belongs to orthorhombic crystal system. The crystalline nature of the BTBN was confirmed by powder X-ray diffraction study. Important functional groups of BTBN were identified by FT-IR spectroscopic analysis. UV-Vis-NIR spectral study showed that the grown crystal is transparent in the entire visible region with low cut off wavelength of 304 nm. BTBN exhibits a SHG efficiency which is nearly 2.38 times higher than that of KDP. The BTBN crystal has high mechanical strength and belongs to soft category, which was confirmed by micorhardness study. The thermal stability of BTBN was determined from TGA and DTA thermal study which revealed that the BTBN crystal has thermal stability up to 243.1 °C. The surface properties and presence of elements was analyzed by SEM and EDAX study, respectively