Effect of Scan Strategies and Use of Support Structures on Surface Quality and Hardness of L-PBF AlSi10Mg Parts

Additive manufacturing allows for a great degree of design freedom and is rapidly becoming a mainstream manufacturing process. However, as in all manufacturing processes, it has its limitations and specificities. Equipping engineers with this knowledge allows for a higher degree of optimization, extracting the most out of this technology. Therefore, a specific part design was devised and created via L-PBF (Laser Powder Bed Fusion) using AlSi10Mg powder. Certain parameters were varied to identify the influence on material density, hardness, roughness, residual stress and microstructures. It was found that on heat treated parts laser pattern strategy is one of the most influential aspects, showing that chessboard and stripes 67° improved outcome; average Ra roughness varied between 8–12 µm, residual stress was higher on vertical surfaces than horizontal surfaces, with the combination of support structures and stripes 67° strategies generating the lowest residual stress (205 MPa on a lateral/vertical face), hardness was non-orientation dependent and larger on samples with chessboard fabrication strategies, while microstructures were composed of α–Al dendrites surrounded by Si particles. The distribution and grain size of the microstructure is dependent on location regarding melt pool and HAZ area. Furthermore, Al–Mg oxides were encountered on the surface, along with pores generating from lack of fusion.The authors would like to acknowledge the Hypermetal Additive Manufacturing for their contribution with some additive manufactured samples and materials, as well as ONA Electro-Erosión Lda. for the use of their electro erosion cutting equipment, used for the separation of certain samples from the build plate. The Authors also would like to thanks to Rui Rocha from CEMUP, due to his sharp critical analysis of SEM results and his help in achieving the best SEM pictures. A.B.P would like to acknowledge the projects UIDB/00481/2020 and UIDP/00481/2020—FCT—Fundação para a Ciencia e a Tecnologia; and CENTRO-01-0145-FEDER-022083—Centro Portugal Regional Operational Programme (Centro2020), under the PORTUGAL 2020 Partnership Agreement, through the European Regional Development Fund.info:eu-repo/semantics/publishedVersio