Sequential Collinear Photofragmentation and Atomic Absorption Spectroscopy for Online Laser Monitoring of Triatomic Metal Species

Industrial chemical processes are struggling with adverse effects, such as corrosion and deposition, caused by gaseous alkali and heavy metal species. Mitigation of these problems requires novel monitoring concepts that provide information on gas-phase chemistry. However, selective optical online monitoring of the most problematic diatomic and triatomic species is challenging due to overlapping spectral features. In this work, a selective, all-optical, in situ gas-phase monitoring technique for triatomic molecules containing metallic atoms was developed and demonstrated with detection of PbCl2. Sequential collinear photofragmentation and atomic absorption spectroscopy (CPFAAS) enables determination of the triatomic PbCl2 concentration through detection of released Pb atoms after two consecutive photofragmentation processes. Absorption cross-sections of PbCl2, PbCl, and Pb were determined experimentally in a laboratory-scale reactor to enable calibration-free quantitative determination of the precursor molecule concentration in an arbitrary environment. Limit of detection for PbCl2 in the laboratory reactor was determined to be 0.25 ppm. Furthermore, the method was introduced for in situ monitoring of PbCl2 concentration in a 120 MWth power plant using demolition wood as its main fuel. In addition to industrial applications, the method can provide information on chemical reaction kinetics of the intermediate species that can be utilized in reaction simulations.publishedVersionPeer reviewe

Fireside corrosion of stainless and low alloyed steels in a waste-fired CFB boiler; The effect of adding sulphur to the fuel

Corrosion field tests have been carried out in the superheater region of a commercial waste-fired 75MW CFBC boiler using air cooled probes. Exposure time was 24 and 1000 hours. The effect of adding sulphur to the fuel on the corrosion of two high alloyed steels and a low alloyed steel was studied. The fuel consisted of 50% household waste and 50% industrial waste. The exposed samples were analyzed by ESEM/EDX and XRD. Metal loss was determined after 1000 hours. Both materials suffered significant corrosion in the absence of sulphur addition and the addition of sulphur to the fuel reduced corrosion significantly. The rapid corrosion of the high alloyed steel in the absence of sulphur addition is caused by the destruction of the chromium-containing protective oxide by formation of calcium chromate. Adding sulphur to the fuel inhibited chromate formation and increased the sulphate/chloride ratio in the deposit. Iron(II) chloride formed on the low alloyed steel regardless of whether sulphur was added or not

Fireside corrosion of stainless and low alloyed steels in a waste-fired CFB boiler; The effect of adding sulphur to the fuel

Corrosion field tests have been carried out in the superheater region of a commercial waste-fired 75MW CFBC boiler using air cooled probes. Exposure time was 24 and 1000 hours. The effect of adding sulphur to the fuel on the corrosion of two high alloyed steels and a low alloyed steel was studied. The fuel consisted of 50% household waste and 50% industrial waste. The exposed samples were analyzed by ESEM/EDX and XRD. Metal loss was determined after 1000 hours. Both materials suffered significant corrosion in the absence of sulphur addition and the addition of sulphur to the fuel reduced corrosion significantly. The rapid corrosion of the high alloyed steel in the absence of sulphur addition is caused by the destruction of the chromium-containing protective oxide by formation of calcium chromate. Adding sulphur to the fuel inhibited chromate formation and increased the sulphate/chloride ratio in the deposit. Iron(II) chloride formed on the low alloyed steel regardless of whether sulphur was added or not