Comparative Corrosion Characterization of Hybrid Zinc Coatings in Cl−-Containing Medium and Artificial Sea Water

The presented investigations demonstrate the corrosion behavior and protective ability of hybrid zinc coatings specially designed for combined protection of low-carbon steel from localized corrosion and biofouling. Polymer-modified copper oxide (CuO) nanoparticles as widely used classic biocide are applied for this purpose, being simultaneously electrodeposited with zinc from electrolytic bath. The corrosion behavior of the hybrid coatings is evaluated in a model corrosive medium of 5% NaCl solution and in artificial sea water (ASW). Scanning electron microscopy (SEM) and atomic force microscopy (AFM) are used to characterize the surface morphology of pure and hybrid zinc coatings. Contact angle measurements are realized with an aim to determine the hydrophobicity of the surface. X-ray photoelectron spectroscopy (XPS) is applied for evaluation of the chemical composition of the surface products appearing as a result of the corrosion treatment. Potentiodynamic polarization (PDP) curves and polarization resistance (Rp) measurements are used to estimate the protective characteristics in both model corrosive media. The results obtained for the hybrid coatings are compared with the corrosion characteristics of ordinary zinc coating with the same thickness. It was found that the hybrid coating improves the anticorrosion behavior of low-carbon steel during the time interval of 35 days and at conditions of external polarization. The tests demonstrate much larger corrosion resistance of the hybrid coating in ASW compared to 5% NaCl solution. The obtained results indicated that the proposed hybrid zinc coating has a potential for antifouling application in marine environment

Protective Characteristics of TiO₂ Sol-Gel Layer Deposited on Zn-Ni or Zn-Co Substrates

This study aimed to present the differences in the corrosion properties and protective ability of two bi-layer systems obtained on low-carbon steel in a model corrosive medium of 5% NaCl solution. These newly developed systems consist of Zn-Co (3 wt.%) or Zn-Ni (10 wt.%) alloy coatings as under-layers and a very thin TiO2 sol-gel film as a top-layer. Scanning electron microscopy (SEM) is used for characterization of the surface morphology of the samples indicating that some quantitative differences appear as a result of the different composition of both zinc alloys. Surface topography is investigated by means of atomic force microscopy (AFM), and the hydrophobic properties are studied by contact angle (CA) measurements. These investigations demonstrate that both sample types possess grain nanometric surface morphology and that the contact angle decreases very slightly. X-ray diffraction (XRD) and X-ray photoelectron spectroscopy (XPS) are used for characterization of the chemical composition and electronic structure of the samples. The roughness Rq of the Zn-Ni/TiO2 is 49.5 nm, while for Zn-Co/TiO2, the Rq value is 53.4 nm. The water contact angels are 93.2 and 95.5 for the Zn-Ni/TiO2 and Zn-Co/TiO2 systems, respectively. These investigations also show that the co-deposition of Zn and Ni forms a coating consisting entirely of Ni2Zn11, while the other alloy contains Zn, Co and the intermetallic compound CoZn13. The corrosion resistance and protective ability are estimated by potentiodynamic polarization (PDP) curves, as well as polarization resistance (Rp) measurements for a prolonged test period (35 days). The results obtained are compared with the corrosion characteristics of ordinary zinc coating with an equal thickness. The experimental data presents the positive influence of the newly developed systems on the enhanced protective properties of low-carbon steel in a test environment causing a localized corrosion—lower corrosion current density of about one magnitude of order (~10−6 A.cm−2 for both systems and ~10−5 A.cm−2 for Zn) and an enhanced protective ability after 35 days (~10,000–17,000 ohms for the systems and ~900 ohms for Zn)

Abstracts Of The Proceedings And The Posters From The Third Scientific Session Of The Medical College Of Varna

October 2-3, 201

50 години Катедра „Социална медицина и организация на здравеопазването`

22 Май 201