Magnetic Properties and AC Losses in AFe2O4 (A = Mn, Co, Ni, Zn) Nanoparticles Synthesized from Nonaqueous Solution

Nanosized particles of AFe2O4 (A = Mn, Co, Ni, or Zn) spinel ferrites were synthesized by coprecipitation from nonaqueous solutions using nitrate salts as starting reagents. The particles were characterized by X-ray diffraction, transmission electron microscopy, and magnetic measurements. Quasistatic magnetic measurements show superparamagnetic behavior with blocking temperature below room temperature for cobalt, nickel, and zinc spinel ferrite nanoparticles. Characteristic magnetic parameters of the particles including average magnetic moment of an individual nanoparticle and blocking temperature have been determined. The specific loss power which is released on the exposure of an ensemble of synthesized particles to a magnetic field is calculated and measured experimentally. It is shown that among all nanoferrites under study, the ZnFe2O4 nanoparticles demonstrate the highest heating efficiency in AC magnetic fields. The key parameters responsible for the heating efficiency in AC magnetic field have been determined. The directions to enhance the SLP value have been outlined

Profound Interfacial Effects in CoFe2O4/Fe3O4 and Fe3O4/CoFe2O4 Core/Shell Nanoparticles

Abstract Two sets of core/shell magnetic nanoparticles, CoFe2O4/Fe3O4 and Fe3O4/CoFe2O4, with a fixed diameter of the core (~ 4.1 and ~ 6.3 nm for the former and latter sets, respectively) and thickness of shells up to 2.5 nm were synthesized from metal chlorides in a diethylene glycol solution. The nanoparticles were characterized by X-ray diffraction, transmission electron microscopy, and magnetic measurements. The analysis of the results of magnetic measurements shows that coating of magnetic nanoparticles with the shells results in two simultaneous effects: first, it modifies the parameters of the core-shell interface, and second, it makes the particles acquire combined features of the core and the shell. The first effect becomes especially prominent when the parameters of core and shell strongly differ from each other. The results obtained are useful for optimizing and tailoring the parameters of core/shell spinel ferrite magnetic nanoparticles for their use in various technological and biomedical applications