Badania nad zaawansowanymi technologiami wytwarzania wyrobów ze stopów Al

The test stands already put in operation and still under development, installed in the Light Metals Division Skawina of the Institute of Non-Ferrous Metals in Gliwice are described. The presentation includes 5MN horizontal direct-indirect extrusion press, 2,5MN vertical forging press, "MeltechConfex MC-260" device for continuous rotary extrusion process, "Melt-Spinning" plant for casting of thin strips, melting-casting plant for Mg alloy billets, heat treatment line, and new testing equipment, including Instron 5582 100 kN and Instron 600DX 600 kN testing machines with attachments for tests carried out at low and high temperatures, automatic hardness tester for HB, HV and HRC hardness measurements, portable X-ray diffractometer for measurement of internal stresses, optical emission spectrometer with channels for the analysis of aluminium and magnesium alloys, STEM 200kV transmission electron microscope, and apparatus for hydrogen content measurement in the solid state. Based on the experimental potential and apparatus available, present research opportunities were discussed and modern trends in the advanced technology of Al and Mg alloys fabrication were outlined.Przedstawiono zainstalowane w Oddziale Metali Lekkich w Skawinie, Instytutu Metali Nieżelaznych w Gliwicach i będące w trakcie realizacji stanowiska doświadczalne (prasę poziomą współbieżno-przeciwbieżną o nacisku 5MN do wyciskania, prasę pionową kuzienną 2,5MN, urządzenie do ciągłego wyciskania na kole "MeltechConfex MC-260", instalację do odlewania cienkich taśm "Melt-Spinnig", stanowisko topielno-odlewnicze wlewków ze stopów Mg, linię obróbki cieplnej) oraz nową aparaturę badawczą (maszyny wytrzymałościowe Instron 5582 100 kN oraz Instron 600DX 600 kN wraz z wyposażeniem do badań w obniżonych i podwyższonych temperaturach, automatyczny twardościomierz do pomiaru twardości metodą HB, HV, HRC, przenośny dyfraktometr rentgenowski do pomiaru naprężeń własnych, emisyjny spektrometr optyczny z kanałami do analizy stopów aluminium i stopów magnezu, transmisyjny mikroskop elektronowy STEM 200 kV, aparat do pomiaru zawartości wodoru w stanie stałym). W oparciu o potencjał doświadczalny i aparaturowy przedstawiono zarówno możliwości badawcze oraz nakreślono nowoczesne kierunki badań w obszarze zaawansowanych technologii stopów Al i Mg

Multilayer metal-ceramic passive armours for helicopters and specjal vehicles

W artykule przedstawiono wyniki badań ostrzałem pancerzy z warstwami o różnych grubościach: płytek ceramicznych (Al2O3, SiC, B4C, AlN), warstw metalowych (aluminiowych, RHA), polietylenu, laminatów lub tkaniny aramidowej. Badano również nowy rodzaj spiekanych płytek z materiałów na bazie faz międzymetalicznych NiAl, wytwarzanych metodą wysokotemperaturowej egzotermicznej reakcji syntezy proszków. Testowane pancerze wytwarzano techniką odlewania lub poprzez łączenie poszczególnych warstw za pomocą klejenia i laminowania. Uzyskano zdolność ochronną przed ostrzałem pociskami przeciwpancernymi kalibru 12.7 mm typu B-32 dla pancerza z płytkami Al2O3, SiC, AlN oraz NiAl10Ni i NiAl10NiSi w osnowie stopu Al. Przeprowadzone badania ostrzałem modeli pasywnego pancerza przestrzennego, z zastosowaniem ceramiki Al2O3, SiC, B4C, (o grubości 8÷10 mm) wykazały skuteczne zatrzymanie 7.62 mm pocisku typu B-32 dla pancerzy o parametrach: grubość ~20 mm, masa 44 kg/m2 dla Al203, 38 kg/m2 dla SiC oraz 32 kg/m2 dla B4C.The article presents the results of firing test of armour reinforced with layers of different thickness made from ceramic plates, metal (aluminium, RHA), polyethylene, laminates, and aramid fabric. Plates of new type sintered from materials based on the intermetallic phases of NiAl produced by high-temperature exothermic reaction of powder synthesis were also studied. The tested armour was made by casting or by joining individual layers with glue and lamination. The strength necessary to protect the armour against firing with B-32 armour piercing projectiles of 12.7 mm calibre was obtained for armour plates made of Al2O3, SiC, AlN, NiAl10Ni and NiAl10NiSi incorporated in an Al alloy matrix. Studies of the firing test of passive spatial armour models made from the Al2O3, SiC, B4C ceramics (with the thickness of 8÷10 mm) showed effective stopping of 7.62mm calibre B-32 AP projectiles in armour of the following parameters: thickness ~ 20 mm, weight 44 kg/m2 for Al203, 38 kg/m2 for SiC and 32 kg/m2 for B4C

Die forging of aluminium alloys from series 2XXX and 4XXX using different types of stock material

Przedstawiono obecne tendencje w zakresie wykorzystywania w procesie kucia matrycowego przygotówek ze stopow Al wytwarzanych różnymi metodami. Zamieszczono wyniki badań wytwarzania odkuwek matrycowych przy zastosowaniu wlewków odlewanych systemem półciągłym w krystalizatorze HOT-TOP ze stopu EN AW-4032 i EN AW-2618A jak również wlewków o strukturze rheocast ze stopu EN AB 42100. W celu uzyskania struktury rheocast wlewki były mieszane mechanicznie i magnetohydrodynamicznie (MHD). Zaprezentowano również wyniki z prob kucia materiałów wytwarzanych z proszkow stopów metodą konsolidacji plastycznej na gorąco na przykładzie stopow AlSi26Ni8 i AlSi26Ni6Fe2. Wykonane przykładowe odkuwki tłoków poddano ocenie struktury oraz właściwości mechanicznych. Opisano rownież najnowsze kierunki badań związane z wykorzystaniem do kucia matrycowego wlewków kształtowych.Recent trends in the application of aluminium alloy stock fabricated by different methods in the process of die forging were presented. The results of the studies on fabrication of die forgings from billets cast in the EN AW- 4032 and EN AW-2618A alloys by semi-continuous process in a HOT-TOP mould were quoted and compared with the results obtained on ingots of a rheocast structure made from the EN AB 42100 alloy. To obtain a rheocast structure, the ingots were subjected to mechanical stirring and to magnetohydrodynamic (MHD) stirring. The results of the trial forging of the stock prepared from alloy powders by the method of hot plastic consolidation were also presented, taking as an example the AlSi26Ni8 and AlSi26Ni6Fe2 alloys. The fabricated pilot forgings of pistons were next examined for their structure and mechanical properties. Recent trends in the research on application of shaped ingots in die forging have been described as well.