Specific heat and magnetocaloric effect in Pr1-xAgxMnO3 manganites

The magnetocaloric effect in alternating magnetic fields has been investigated in Pr1-xAgxMnO3 manganites with x=0.05-0.25. The stepwise reversal of the sign of the magnetocaloric effect has been revealed in a weakly doped sample (x=0.05) at low temperatures (~80 K). This reversal is attributed to the coexistence of the ferromagnetic and canted antiferromagnetic phases with different critical temperatures.Comment: 4 pages, 4 figure

Evolution of microstructural and mechanical properties of nanocrystalline Co2FeAl Heusler alloy prepared by mechanical alloying

Mechanical alloying (MA) has been used to fabricate the Co2FeAl Heusler alloy with a nanocrystalline structure. The formation mechanism of the alloy has been investigated. Rietveld analysis showed that all samples that were milled for more than 15 hours had an L21 structure with a space group of Fm3m. The crystallite size and internal strain of the samples were calculated using the Williamson-Hall equation. With mechanical alloying of up to 20 hours the crystallite size of Co2FeAl increased, after which the crystallite size started to decrease. In contrast, internal strain first decreased during the process and then increased with the increase of milling time. The powder obtained after 20 hours of MA was split into three parts and separately annealed at 300, 500 and 700 oC for 5 hours. A considerable increase was observed in the hardness value of powder particles with the increase of annealing temperature up to 500 oC. However, the hardness value of the sample annealed at 700 oC decreased. It seems that this feature is related to parameters such as increase of crystallite size, enhancement of lattice ordering, change in density of defects and impurities and nonstoichiometric effects