Improvement of critical current in MgB2/Fe wires by a ferromagnetic sheath

Transport critical current (Ic) was measured for Fe-sheathed MgB2 round wires. A critical current density of 5.3 x 10^4 A/cm^2 was obtained at 32K. Strong magnetic shielding by the iron sheath was observed, resulting in a decrease in Ic by only 15% in a field of 0.6T at 32K. In addition to shielding, interaction between the iron sheath and the superconductor resulted in a constant Ic between 0.2 and 0.6T. This was well beyond the maximum field for effective shielding of 0.2T. This effect can be used to substantially improve the field performance of MgB2/Fe wires at fields at least 3 times higher than the range allowed by mere magnetic shielding by the iron sheath. The dependence of Ic on the angle between field and current showed that the transport current does not flow straight across the wire, but meanders between the grains

Pigment Melanin: Pattern for Iris Recognition

Recognition of iris based on Visible Light (VL) imaging is a difficult problem because of the light reflection from the cornea. Nonetheless, pigment melanin provides a rich feature source in VL, unavailable in Near-Infrared (NIR) imaging. This is due to biological spectroscopy of eumelanin, a chemical not stimulated in NIR. In this case, a plausible solution to observe such patterns may be provided by an adaptive procedure using a variational technique on the image histogram. To describe the patterns, a shape analysis method is used to derive feature-code for each subject. An important question is how much the melanin patterns, extracted from VL, are independent of iris texture in NIR. With this question in mind, the present investigation proposes fusion of features extracted from NIR and VL to boost the recognition performance. We have collected our own database (UTIRIS) consisting of both NIR and VL images of 158 eyes of 79 individuals. This investigation demonstrates that the proposed algorithm is highly sensitive to the patterns of cromophores and improves the iris recognition rate.Comment: To be Published on Special Issue on Biometrics, IEEE Transaction on Instruments and Measurements, Volume 59, Issue number 4, April 201

Carbon-substitution effect on the electronic properties of MgB2_2 single crystals

The electronic properties of the carbon substituted MgB$_2$ single crystals are reported. The carbon substitution drops T$_c$ below 2 K. In-plane resistivity shows a remarkable increase in residual resistivity by C-substitution, while the change of in-plane/out-of-plane Hall coefficients is rather small. Raman scattering spectra indicate that the E$_{2g}$-phonon frequency radically hardens with increasing the carbon-content, suggesting the weakening of electron-phonon coupling. Another striking C-effect is the increases of the second critical fields in both in-plane and out-of-plane directions, accompanied by a reduction in the anisotropy ratio. The possible changes in the electronic state and the origin of T$_c$-suppression by C-substitution are discussed.Comment: 6 pages, 8 figure

Superconducting screening on different length scales in high-quality bulk MgB2 superconductor

High quality bulk MgB2 exhibit a structure of voids and agglomeration of crystals on different length-scales. Because of this, the superconducting currents percolate between the voids in the ensuing structure. Magnetic measurements reveal that the superconducting currents circulate on at least three different length-scales, of ~1 micrometre, ~10 micrometre and whole of the sample (~millimetre). Each of these screenings contributes to the measured irreversible magnetic moment (Dm). The analysis of the field dependence of Dm for samples of subsequently decreasing size showed that the critical current obtained using the simple critical state model is erroneous. This leads to the artefact of the sample size-dependent critical current and irreversibility field. Our data analysis enables the separation of the contribution of each of the screening currents to Dm. The field dependence of each of the currents follows a stretched exponential form. The currents flowing around whole of the sample give a dominant contribution to Dm in the intermediate fields (1T < H < 4T at 20K) and they can be used to obtain the value of Jc from critical state model, which corresponds to the transport Jc

Proposal of a Reflector-Enhanced Solar Still Concept and Its Comparison with Conventional Solar Stills

Water scarcity is a global concern and poses significant problems to countries with arid and semi-arid climates, like Iran. Considering financial difficulties, a lack of knowledge about high-tech alternatives, low incomes, a lack of access to high-tech tools, and low maintenance capabilities in developing countries, solar still desalination is a decent technology for providing proper water, especially for rural areas. However, the low water-production rate using this method dictates a very vast area requirement for solar still farms in order to provide significant amounts of water. In this research, we proposed a mirror-enhanced solar still and mathematically compared its water-production rate to that of conventional ones. In comparison to conventional solar stills, our proposed reflector-enhanced solar still benefits from several improvements, including lower glass temperatures, increased water basing temperatures, and receiving much more solar irradiation. Hence, the proposed system can increase water production from 7.5 L/day to 24 L/day. The results showed that the proposed method is highly effective and could be used in field-scale projects in arid and semi-arid climates

Transport critical current of Solenoidal MgB2/Cu Coils Fabricated Using a Wind-Reaction In-situ Technique

In this letter, we report the results of transport Jc of solenoid coils upto 100 turns fabricated with Cu-sheathed MgB2 wires using a wind-reaction in-situ technique. Despite the low density of single core and some reaction between Mg and Cu-sheath, our results demonstrate the decrease in transport Jc with increasing length of MgB2 wires is insignificant. Solenoid coils with diameter as small as 10 mm can be readily fabricated using a wind-reaction in-situ technique. The Jc of coils is essentially the same as in the form of straight wires. A Jc of 133,000 A/cm2 and 125,000 A/cm2 at 4 K and self field has been achieved for a small coil wound using Cu-sheathed tape and Cu-sheathed wire respectively. These results indicate that the MgB2 wires have a great potential for lage scale applicationsComment: 6 pages, 4 figures, 1 tabl

Very fast formation of superconducting MgB2/Fe wires with high Jc

In this paper we have investigated the effects of sintering time and temperature on the formation and critical current densities of Fe-clad MgB2 wires. MgB2 wires were fabricated using the powder-in-tube process and sintered for different periods of time at predetermined temperatures. All the samples were examined using XRD, SEM and magnetisation measurements. In contrast to the common practice of sintering for several hours, the present results show that there is no need for prolonged heat treatment in the fabrication of Fe-clad MgB2 wires. A total time in the furnace of several minutes is more than enough to form nearly pure MgB2 with high performance characteristics. The results from Tc, Jc and Hirr show convincingly that the samples which were sintered for 3 minutes above 800 oC are as good as those sintered for longer times. In fact, the Jc field performance for the most rapidly sintered sample is slightly better than for all other samples. Jc of 4.5 times 10 ^5 A/cm2 in zero field and above 10 ^5 A/cm2 in 2T at 15 K has been achieved for the best Fe-clad MgB2 wires. As a result of such a short sintering there is no need for using high purity argon protection and it is possible to carry out the heat treatment in a much less protective atmosphere or in air. These findings substantially simplify the fabrication process, making it possible to have a continuous process for fabrication and reducing the costs for large-scale production of MgB2 wires.Comment: 15 pages, one table, 9 figures, submitted to Physica C on June 8, 200