Reducing tin droplet ejection from capillary porous structures under hydrogen plasma exposure in Magnum-PSI

Liquid metal based divertors could be a more robust alternative to a solid tungsten design for DEMO. The liquid is confined in a sponge-like tungsten layer, called a capillary porous structure (CPS). It has been found previously that under certain conditions, many tin droplets eject from a CPS when it is brought into contact with a hydrogen plasma. These would present a contamination issue for the plasma core. Stability analysis suggests that droplet ejection can be suppressed by reduction of the pore size. To test this, stainless-steel CPS targets with pore size ranging from 0.5–100µm filled with tin were exposed to identical loading conditions. This was done in the linear plasma device Magnum-PSI, capable of reaching divertor relevant plasma conditions. Furthermore, the influence of the CPS manufacturing techniques is considered by comparing the performance of a 3D printed, a mesh felts and a sintered CPS, all made from tungsten. Each target was surrounded by four witness plates, which were analysed post-mortem for Sn content by Rutherford backscattering. During plasma exposure, tin droplets were observed using a fast visible camera and plasma light emission via survey optical emission spectroscopy. The results imply that Sn erosion can be reduced by a factor of 50 when reducing the pore size. Moreover, it highlights the importance of avoiding overfilling of CPS targets with Sn

Reducing tin droplet ejection from capillary porous structures under hydrogen plasma exposure in Magnum-PSI

Liquid metal based divertors could be a more robust alternative to a solid tungsten design for DEMO. The liquid is confined in a sponge-like tungsten layer, called a capillary porous structure (CPS). It has been found previously that under certain conditions, many tin droplets eject from a CPS when it is brought into contact with a hydrogen plasma. These would present a contamination issue for the plasma core. Stability analysis suggests that droplet ejection can be suppressed by reduction of the pore size. To test this, stainless-steel CPS targets with pore size ranging from 0.5-100um filled with tin were exposed to identical loading conditions. This was done in the linear plasma device Magnum-PSI, capable of reaching divertor relevant plasma conditions. Furthermore, the influence of the CPS manufacturing techniques is considered by comparing the performance of a 3D printed, a mesh felts and a sintered CPS, all made from tungsten. Each target was surrounded by four witness plates, which were analysed post-mortem for Sn content by Rutherford backscattering. During plasma exposure, tin droplets were observed using a fast visible camera and plasma light emission via survey optical emission spectroscopy. The results imply that Sn erosion can be reduced by a factor of 50 when reducing the pore size. Moreover, it highlights the importance of avoiding overfilling of CPS targets with Sn

Reducing tin droplet ejection from capillary porous structures under hydrogen plasma exposure in Magnum-PSI

Liquid metal based divertors could be a more robust alternative to a solid tungsten design for DEMO. The liquid is confined in a sponge-like tungsten layer, called a capillary porous structure (CPS). It has been found previously that under certain conditions, many tin droplets eject from a CPS when it is brought into contact with a hydrogen plasma. These would present a contamination issue for the plasma core. Stability analysis suggests that droplet ejection can be suppressed by reduction of the pore size. To test this, stainless-steel CPS targets with pore size ranging from 0.5-100um filled with tin were exposed to identical loading conditions. This was done in the linear plasma device Magnum-PSI, capable of reaching divertor relevant plasma conditions. Furthermore, the influence of the CPS manufacturing techniques is considered by comparing the performance of a 3D printed, a mesh felts and a sintered CPS, all made from tungsten. Each target was surrounded by four witness plates, which were analysed post-mortem for Sn content by Rutherford backscattering. During plasma exposure, tin droplets were observed using a fast visible camera and plasma light emission via survey optical emission spectroscopy. The results imply that Sn erosion can be reduced by a factor of 50 when reducing the pore size. Moreover, it highlights the importance of avoiding overfilling of CPS targets with Sn