Electrochemical oxidation of methanol on Pt3Co bulk alloy

The electrochemical oxidation of methanol was investigated on a Pt3Co bulk alloy in acid solutions. Kinetic parameters such as transfer coefficient, reaction orders with respect to methanol and H+ ions and energy of activation were determined. It was found that the rate of methanol oxidation is significantly diminished by rotation of the electrode. This effect was attributed to the diffusion of formaldehyde and formic acid from the electrode surface. Stirring of the electrolyte also influenced the kinetic parameters of the reaction. It was speculated that the predominant reaction pathway and rate determining step are different in the quiescent and in the stirred electrolyte. Cobalt did not show a promoting effect on the rate of methanol oxidation on the Pt3Co bulk alloy with respect to a pure Pt surface

Mixtures of methanol and 2-propanol as a potential fuel for direct alcohol fuel cells

The electrochemical oxidation of methanol, 2-propanol, and their mixtures was investigated on a Pt/C thin film electrode in acid solution. It was confirmed that the oxidation of 2-propanol commences at less positive potentials than that of methanol and exhibits significantly higher oxidation current densities at low potentials. When both methanol and 2-propanol were present in the solution, the onset of the oxidation current was the same as for the oxidation of pure 2-propanol. Although both alcohols inhibit the oxidation reaction of each other to a certain extent, steady-state polarization measurements showed that their mixture provides higher current densities than single alcohols over the entire potential region from the hydrogen region to oxide formation on the Pt surface. This implies that the addition of 2-propanol into the fuel may extend the operational range of direct methanol fuel cells

Methanol oxidation at platinum electrodes in acid solution: comparison between model and real catalysts

Methanol oxidation in acid solution was studied at platinum single crystals, Pt(hkl), as the model catalyst, and at nanostructural platinum supported on high surface area carbon, Pt/C, as the real catalyst. The linear extrapolation method was used to determine the beginning of hydroxyl anion adsorption. Structural sensitivity of the adsorption was proved and a correlation with the onset of the methanol oxidation current was established at all catalysts. Bisulfate and chloride anions were found to decrease the methanol oxidation rate, but probably did not influence the reaction parth. The specific activity for the reaction increased in the sequence Pt(110) < Pt/C < Pt(111), suggesting that the activity of the supported Pt catalyst can be correlated with the activities of the dominating crystal planes on its surface