2 research outputs found
The Influence of Intralayer Porosity and Phase Transition on Corrosion Fatigue of Additively Manufactured 316L Stainless Steel Obtained by Direct Energy Deposition Process
A direct energy deposition (DED) process using wires is considered an additive manufacturing technology that can produce large components at an affordable cost. However, the high deposition rate of the DED process is usually accompanied by poor surface quality and inherent printing defects. These imperfections can have a detrimental effect on fatigue endurance and corrosion fatigue resistance. The aim of this study was to evaluate the critical effect of phase transition and printing defects on the corrosion fatigue behavior of 316L stainless steel produced by a wire laser additive manufacturing (WLAM) process. For comparison, a standard AISI 316L stainless steel with a regular austenitic microstructure was studied as a counterpart alloy. The structural assessment of printing defects was performed using a three-dimensional non-destructive method in the form of X-ray microtomography (CT) analysis. The microstructure was evaluated by optical and scanning electron microscopy, while general electrochemical characteristics and corrosion performance were assessed by cyclic potentiodynamic polarization (CCP) analysis and immersion tests. The fatigue endurance in air and in a simulated corrosive environment was examined using a rotating fatigue setup. The obtained results clearly demonstrate the inferior corrosion fatigue endurance of the 316L alloy produced by the WLAM process compared to its AISI counterpart alloy. This was mainly related to the drawbacks of WLAM alloys in terms of having a duplex microstructure (austenitic matrix and secondary delta-ferrite phase), reduced passivity, and a significantly increased amount of intralayer porosity that acts as a stress intensifier of fatigue cracking
The Effect of a Slow Strain Rate on the Stress Corrosion Resistance of Austenitic Stainless Steel Produced by the Wire Laser Additive Manufacturing Process
The wire laser additive manufacturing (WLAM) process is considered a direct-energy deposition method that aims at addressing the need to produce large components having relatively simple geometrics at an affordable cost. This additive manufacturing (AM) process uses wires as raw materials instead of powders and is capable of reaching a deposition rate of up to 3 kg/h, compared with only 0.1 kg/h with common powder bed fusion (PBF) processes. Despite the attractiveness of the WLAM process, there has been only limited research on this technique. In particular, the stress corrosion properties of components produced by this technology have not been the subject of much study. The current study aims at evaluating the effect of a slow strain rate on the stress corrosion resistance of 316L stainless steel produced by the WLAM process in comparison with its counterpart: AISI 316L alloy. Microstructure examination was carried out using optical microscopy, scanning electron microscopy (SEM) and X-ray diffraction analysis, while the mechanical properties were evaluated using tensile strength and hardness measurements. The general corrosion resistance was examined by potentiodynamic polarization and impedance spectroscopy analysis, while the stress corrosion performance was assessed by slow strain rate testing (SSRT) in a 3.5% NaCl solution at ambient temperature. The attained results highlight the inferior mechanical properties, corrosion resistance and stress corrosion performance, especially at a slow strain rate, of the WLAM samples compared with the regular AISI 316L alloy. The differences between the WLAM alloy and AISI 316L alloy were mainly attributed to their dissimilarities in terms of phase compositions, structural morphology and inherent defects