The Residual Stress Relaxation Behavior of Weldments During Cyclic Loading
Accurate measurement of residual stress is necessary to obtain reliable predictions of fatigue lifetime and enable estimation of time-to-facture for any given stress level. In this article, relaxation of welding residual stresses as a function of cyclic loading was documented on three common steels: AISI 1008, ASTM A572, and AISI 4142. Welded specimens were subjected to cyclic bending (R = 0.1) at different applied stresses, and the residual stress relaxation existing near the welds was measured as a function of cycles. The steels exhibited very different stress relaxation behaviors during cyclic loadings, which can be related to the differences in the microstructures of the specimens. A phenomenological model, which treats dislocation motion during cyclic loading as being analogous to creep of dislocations, is proposed for estimation of the residual stress relaxation
Recommended from our members
Fatigue Crack Growth Mechanisms At the Microstructure Scale in Al-Si-Mg Cast Alloys: Mechanisms in Regions II and III
The fatigue crack growth behavior in Regions 11 and III of crack growth was investigated for hypoeutectic and eutectic Al-Si-Mg cast alloys. To isolate and establish the mechanistic contributions of characteristic microstructural features (dendritic α-Al matrix, eutectic phases, Mg-Si strengthening precipitates), alloys with various Si content/morphology, grain size level, and matrix strength were studied; the effect of secondary dendrite arm spacing (SDAS) was also assessed. In Regions 11 and III of crack growth, the observed changes in the fracture surface appearance were associated with changes in crack growth mechanisms at the microstructural scale (from a linear advance predominantly through primary α-Al to a tortuous advance exclusively through AI-Si eutectic Regions). The extent of the plastic zone ahead of the crack tip was successfully used to explain the changes in growth mechanisms. The fatigue crack growth tests were conducted on compact tension specimens under constant stress ratio, R = 0.1, in ambient conditions