Strontium Substituted Tricalcium Phosphate Bone Cement: Short and Long‐Term Time‐Resolved Studies and In Vitro Properties

Due to a significant influence of strontium (Sr) on bone regeneration, Sr substituted beta-tricalcium phosphate (Sr-TCP) cement is prepared and investigated by short- and long-term time-resolved techniques. For short-term investigations, energy-dispersive X-ray diffraction, infrared spectroscopy, and, for the first time, terahertz time-domain spectroscopy techniques are applied. For long-term time-resolved studies, angular dispersive X-ray diffraction, scanning electron microscopy, mechanical tests, and behavior in Ringer solution are carried out. After 45 min of the cement setting, the Sr-TCP phase is no longer detectable. During this time period, an appearance and constant increase of the final brushite phase are registered. The compressive strength of the Sr-TCP cement increases from 4.5 MPa after 2 h of setting and reaches maximum at 13.3 MPa after 21 d. After cement soaking for 21 d in Ringer solution, apatite final product, with an admixture of brushite and TCP phases is detected. The cytotoxicity aspects of the prepared cement are investigated using NCTC 3T3 fibroblast cell line, and the cytocompatibility-by human dental pulp mesenchymal stem cells. The obtained results allow to conclude that the developed Sr-TCP cement is promising for biomedical applications for bone tissue

Ceramics based on calcium pyrophosphate nanopowders

Present work is aimed at the fabrication of resorbable bioceramics based on calcium pyrophosphate (CPP) from the synthesized powders of amorphous hydrated calcium pyrophosphate (AHCPP). Amorphous hydratedcalcium pyrophosphate in the form of nanopowders was precipitated from Ca(NO3 )2 and (NH4 )4P2O7 solutions at room temperature in the presence of PO3– ions. Crystalline CPP powder was fabricated from AHCPP by its thermal decomposition at 600 °C and consisted of β- and α- phase. Small particles, with the size less than 200 nm, were formed promoting sintering of the ceramic material. The final sample, sintered at 900 °C, exhibits microstructure with submicron grains, apparent density of 87% of theoretical density (TD) and demonstrates tensile strength of 70 MPa