3 research outputs found
Aging of Bitumen and Asphalt Concrete: Comparing State of the Practice and Ongoing Developments in the United States and Europe
Aging is a crucial factor in pavement performance and being able to determine its effect on a mixture is necessary to link its initial properties to the properties over time in order to ensure the intended service life. This is becoming more important now that climate change leads to increased variation in weather conditions, while environmental considerations cause changes in the constituent materials that are used. As a result, past experience is becoming less reliable. In this paper, the USA and European approaches to aging are compared, showing that those contain the same test equipment and almost identical conditions for aging. This allows the exchange of data and experience. The current tests are suitable for binders and give an indication of the sensitivity to aging. For short term aging, Rolling Thin Film Oven Test (RTFOT) conditioning gives a reasonable indication of bitumen aging during asphalt concrete production and construction. This only holds for penetration grade binders during hot mix production and construction. For long term aging, because of the many variables involved, developing a single test method to characterize aging sensitivity seems impossible. However, using more elaborate protocols in existing, practical tests can provide more information and the necessary input for kinetic aging expressions. A pressure aging vessel (PAV) protocol for testing at two temperatures and time intervals, specifically at 90 and 100 degrees Celsius and for 20 and 40 hours, respectively, is suggested. Using the same conditioning in characterizing materials for pavement construction and research will facilitate the exchange of data and enable faster developments.Alternate title: Review of Asphalt (Concrete) Aging Tests in the US and Europe.Pavement Engineerin
Aging of Asphalt Symposium, September 17th 2014, Delft, the Netherlands
Technical specifications for the asphalt concrete properties are developed to be able to specify mixtures that will perform well in pavement applications. Being able to identify and determine properties related to pavement performance in practice is crucial for both road authorities and contractors, since it allows for design and risk management by determining design life times and reliability. However, the properties of Asphalt Concrete (AC) change over its lifetime and since most pavement layers last for a decade or more these changes are crucial in determining the performance in practice. For many of the standard materials the effect of aging is implicitly dealt with in the safety factors that also account for other effects such as the variation rest periods/healing and variations in traffic and weather in the design methods and specifications. Rapid changes in the materials used (increasing percentages reclaimed asphalt, bio-bitumen, rejuvenators, waste materials) and in the production of both bitumen (new refining methods resulting in different composition of bitumen) and asphalt concrete itself (warm mix asphalt, porous asphalt concrete, rubber asphalt mixtures) lead to increased uncertainty in the effects of aging. As a result, the uncertainties in pavement performance increase, which means the prediction of maintenance and the necessary budgets is getting more inaccurate. In order to maintain the ability to reliably design and maintain pavements and determine the most cost-effective solutions for a given situation, a better understanding of the aging processes and objective methods to take into account aging effects on material properties is needed. This need is widely recognized, in the USA the Mechanical Empirical Design Guide takes aging into account through aging tests on the bitumen used and in Europe CEN TC227 works on establishing a method to assess the aging sensitivity of asphalt mixtures. This symposium aimed at combining the existing information and insights from ongoing research into recommendations that will allow the development of methods to determine aging sensitivity and the impact on pavement performance, facilitate the exchange of obtained data and stimulate further developments The resulting recommendations are: \u95Do make long term aging sensitivity of binders part of the bitumen standards and take the results from the aging sensitivity of binders into consideration when assessing AC properties. Be aware that RTFOT testing only gives an indication of the sensitivity of a penetration grade binder to aging during hot mix production and construction, it doesn’t work for hard grades, PMB’s or warm mixes. \u95Because of the many variables involved, developing one test method to characterise aging sensitivity seems improbable. However, PAV aging is both practical and, if tests at various conditions are carried out, able to give kinematic properties. A PAV protocol for testing at two temperatures and time intervals could provide practical characterisation information for the short term and enable model development and validation on the long term. RCAT and other aging procedures could also be used in this sense, but considering the availability of equipment and the wide spread experience, PAV is the best candidate to allow the rapid development of international experience with the approach. Based on the current standards and the work presented during the symposium, PAV tests at 90 and 100 degrees Celsius and 20 and 40 hours, respectively, are suggested. The low values for temperature and duration are based on the current standards and fit both the USA and CEN procedure, while research shows that after 40 hours at 100 degrees the chemical (FTIR) and rheological (DSR) properties of laboratory aged and field samples were similar (Section 6.5 and 8.5). At 100oC the temperature is low enough so that the effect of secondary reactions is negligible. As such, these conditions are appropriate for kinetic expressions for in service pavement performance. For high temperature processes and possibly also for repeated recycling (very long term) more sophisticated methods are needed. \u95Set-up and maintain field monitoring of temperature and UV radiation in various climate zones, as well as regular sampling over time and height to keep checking the predicted changes (from both tests and models), versus the actual changes in properties order to ensure reliability of the data as well as the applicability for pavement performance prediction. In setting up field tests, it is important to get both the composition of the virgin bitumen and the composition after mixing, transport and placement in the pavement. These compositions provide the starting points from both the material and pavement structure point of view and can be used to assess the development of aging products over time. There is a lot of discussion about the impact of binder recovery methods on the observed composition, so until it is proven that this does not have an influence, for comparisons the same recovery method should be used. \u95Set up a coordination and support action on AC-Aging to continue to exchange information and experiences, both in research and in construction projects. \u95develop an IR testing protocol, to facilitate the exchange of results and information. \u95Compare the bitumen composition that is found through various recovery methods to establish if there is an effect and if so, develop a procedure to address this. \u95To further understanding of aging, a Round Robin test on the differences in test conditions between US and EU, allowing better access to each other’s data and knowledge would be useful. \u95When developing aging tests for AC, it would be useful to look at the US experience. As long as there is no fundamentally correct method for assessing the aging, it would be preferable to standardize it as much as possible in order to allow cooperation and exchange of data.Structural EngineeringCivil Engineering and Geoscience
Bituminous Binder and Bituminous Mixture Modified with Waste Polyethylene
RILEM TC-279 WMR task group TG 1 studied the performance of waste Polyethylene (PE) in bituminous binders and bituminous mixtures. Several laboratories participated in this study following a common protocol. Locally sources aggregates and bituminous binder and same source of waste PE were utilized. The binder experiments showed that at high temperatures, using MSCR tests, PE modified blends had better resistance to permanent deformation in comparison to the non modified binder. Whereas at intermediate temperatures, using the LAS tests, fatigue performance of the PE blends could withstand more loading cycles under low strains; however, it could sustain less loading cycles under high strains due to the increase in brittleness. Dry process was used for the mixture experiments in order to bypass the stability and inhomogeneity experience that was observed at the binder scale. The PE modified mixtures showed improved workability and increased strength. The higher the PE dosage, the higher the ITS increase with respect to the values measured for the control materials (i.e., without any plastic waste) thanks to the improved cohesion of the plastic modified mastic. The stiffness experiments tended to show an improved performance with a lower time dependence and a higher elasticity when plastic was added. The cyclic compression tests demonstrated a reduced creep rate along with a higher creep modulus thanks to the addition of PE; similar conclusions can be drawn from the experimental findings coming from wheel tracking test. Furthermore, acceptable and often improved moisture resistance was observed for PE modified materials.Green Open Access added to TU Delft Institutional Repository ‘You share, we take care!’ – Taverne project https://www.openaccess.nl/en/you-share-we-take-care Otherwise as indicated in the copyright section: the publisher is the copyright holder of this work and the author uses the Dutch legislation to make this work public.Pavement Engineerin