Screen printed barium titanate thick films prepared from mechanically activated powders

Barium titanate thick films were prepared from mechanically activated powders based on BaCO3 and TiO2. The thick films were screen-printed on alumina substrates electroded with Ag/Pd. The BT films were sintered at 850°C for 1 hour. The thickness was 30-75 μm depending of number of layers. The microstructure of thick films and the compatibility between BT layers and substrate was investigated by SEM. The dielectric properties were measured and the results were reported

Screen printed barium titanate thick films prepared from mechanically activated powders

Barium titanate thick films were prepared from mechanically activated powders based on BaCO3 and TiO2. The thick films were screen-printed on alumina substrates electroded with Ag/Pd. The BT films were sintered at 850°C for 1 hour. The thickness was 30-75 μm depending of number of layers. The microstructure of thick films and the compatibility between BT layers and substrate was investigated by SEM. The dielectric properties were measured and the results were reported