Drastic improvement of surface structure and current-carrying ability in YBa2Cu3O7 films by introducing multilayered structure

Much smoother surfaces and significantly improved superconducting properties of relatively thick YBa2Cu3O7 (YBCO) films have been achieved by introducing a multilayered structure with alternating main YBCO and additional NdBCO layers. The surface of thick (1 microm) multilayers has almost no holes compared to YBCO films. Critical current density (Jc) have been drastically increased up to a factor > 3 in 1 microm multilayered structures compared to YBCO films over entire temperature and applied magnetic filed range. Moreover, Jc values measured in thick multilayers are even larger than in much thinner YBCO films. The Jc and surface improvement have been analysed and attributed to growth conditions and corresponding structural peculiarities.Comment: Accepted to Appl. Phys. Lett. 88, June (2006), in press 4 pages, 3 figure

Myths of the High Medical Cost of Old Age and Dying

The rising costs of medical care in the United States are often erroneously linked to the growing population of older adults. Despite public perception, health care costs associated with aging are limited. Part of the ILC-USA's project on Ageism In America with generous support from the Open Society Institute, this report identifies and dispels seven myths about caring for older people at the end of life

Nodeless superconductivity in Ir1−x_{1-x}Ptx_xTe2_2 with strong spin-orbital coupling

The thermal conductivity $\kappa$ of superconductor Ir$_{1-x}$Pt$_{x}$Te$_2$ ($x$ = 0.05) single crystal with strong spin-orbital coupling was measured down to 50 mK. The residual linear term $\kappa_0/T$ is negligible in zero magnetic field. In low magnetic field, $\kappa_0/T$ shows a slow field dependence. These results demonstrate that the superconducting gap of Ir$_{1-x}$Pt$_{x}$Te$_2$ is nodeless, and the pairing symmetry is likely conventional s-wave, despite the existence of strong spin-orbital coupling and a quantum critical point.Comment: 5 pages, 4 figure

Work Function of Single-wall Silicon Carbide Nanotube

Using first-principles calculations, we study the work function of single wall silicon carbide nanotube (SiCNT). The work function is found to be highly dependent on the tube chirality and diameter. It increases with decreasing the tube diameter. The work function of zigzag SiCNT is always larger than that of armchair SiCNT. We reveal that the difference between the work function of zigzag and armchair SiCNT comes from their different intrinsic electronic structures, for which the singly degenerate energy band above the Fermi level of zigzag SiCNT is specifically responsible. Our finding offers potential usages of SiCNT in field-emission devices.Comment: 3 pages, 3 figure