Evaluation of the surface hardness of composite resins before and after polishing at different times

PURPOSE: The aim of this study was to evaluate the surface hardness of six composite resins: Revolution, Natural Flow, Fill Magic Flow, Flow-it! (flowables), Silux Plus (microfilled) and Z100 (minifilled) before and after polishing at different times. MATERIALS AND METHODS: For this purpose, 240 specimens (5mm diameter, 1.4mm high) were prepared. Vickers hardness was determined before and after polishing at different times: immediately, 24h, 7 and 21 days after preparation of the samples. Statistical analysis was performed by ANOVA and Tukey test. RESULTS: There was no difference in the hardness of flowable resins, which had lower hardness than the minifilled resin. The minifilled resin showed the highest surface hardness as compared to the other materials (pPROPOSIÇÃO: O objetivo deste estudo foi avaliar a dureza superficial de seis resinas compostas - Revolution, Natural Flow, Fill Magic Flow, Flow-it! (flowables), Silux Plus (micropartículas) e Z100 (híbrida) - antes e após o polimento realizado em diferentes tempos. MATERIAL E MÉTODO: Foram confeccionados 240 corpos-de-prova circulares (5mm de diâmetro e 1,4mm de altura). A dureza Vickers foi obtida antes e após o polimento realizado em diferentes tempos: imediatamente, 24 horas, 7 dias e 21 dias após a confecção do corpo-de-prova. Os dados foram analisados estatisticamente por meio da ANOVA e do Teste de Tukey. RESULTADOS: Não houve diferença entre as resinas compostas flowable, as quais apresentaram os menores valores de dureza. A resina composta híbrida demonstrou os melhores resultados. Todos os materiais exibiram aumento de dureza após a realização do polimento, que foi mais evidente após 7 dias. CONCLUSÃO: Pôde-se concluir que, independente do tipo de resina composta, a dureza superficial foi consideravelmente maior quando o polimento foi realizado 1 semana após a confecção dos corpos-de-prova

Influence of light-curing unit systems on shear bond strength and marginal microleakage of composite resin restorations

The aim of the present study was to evaluate the influence of different photopolymerization (halogen, halogen soft-start and LED) systems on shear bond strength (SBS) and marginal microleakage of composite resin restorations. Forty Class V cavities (enamel and dentin margins) were prepared for microleakage assessment, and 160 enamel and dentin fragments were prepared for the SBS test, and divided into 4 groups. Kruskal-Wallis and Wilcoxon tests showed statistically significant difference in microleakage between the margins (p < 0.01) with incisal margins presenting the lowest values. Among the groups, it was observed that, only at the cervical margin, halogen soft-start photo polymerization presented statistically significant higher microleakage values. For SBS test, ANOVA showed no statistical difference (p > 0.05) neither between substrates nor among groups. It was concluded that Soft-Start technique with high intensity end-light influenced negatively the cervical marginal sealing, but the light-curing systems did not influence adhesion.Coordenacao de Aperfeicoamento de Pessoal de Nivel Superior (CAPES)FAPES

Efeito do ácido clorídrico gasoso no esmalte humano e bovino

Objetivo: Avaliar a ação do ácido clorídrico gasoso sobre o esmalte humano e bovino e comparar o padrão de desmineralização desses substratos expostos ao agente erosivo gasoso. Métodos: Oito espécimes de esmalte bovino e oito de esmalte humano foram obtidos (4 × 4 × 2 mm), metade da superfície foi protegida com resina composta e a outra metade exposta ao ácido clorídrico gasoso (gHCl), pH 2 a 37 °C, por 3 min, 8 vezes ao dia, durante 12 dias, e em intervalos os espécimes foram mantidos em saliva artificial. Os espécimes foram analisados quanto ao perfil de desgaste, rugosidade superficial e microdureza (antes e após a exposição ao ácido). Os dados foram analisados estatisticamente por ANOVA de uma via. Resultados: Os dados não mostraram diferença significativa entre o esmalte bovino e humano para todas as propriedades analisadas – microdureza (98,1 ± 5,2, 96,9 ± 4,8), perfil de desgaste (11,5 ± 2,8, 11,4 ± 3,6) e rugosidade (2,6 ± 0,3, 3,3 ± 0,3), respectivamente. Nas imagens, observou-se que gHCl pode causar erosão do esmalte em ambos os grupos. Conclusão: O ácido clorídrico gasoso causa erosão do esmalte de forma semelhante em bovinos e humanos.Objective: To evaluate the action of gaseous hydrochloric acid on human and bovine enamel and compare the demineralization pattern of these substrates exposed to the gaseous erosive agent. Methods: Eight bovine enamel and eight human enamel specimens were obtained (4 × 4 × 2 mm), half surface was protected with composite resin and the other half was exposed to gaseous hydrochloric acid (gHCl), pH 2 at 37 °C, for 3 min, 8 times a day, for 12 days, and in intervals the specimens were maintained in artificial saliva. The specimens were analyzed according to wear profile, surface roughness and microhardness (before and after acid exposition). Data were statistically analyzed by one-way ANOVA. Results: Data showed no significant difference between bovine and human enamel for all properties analyzed – microhardness (98.1 ± 5.2, 96.9 ± 4.8), wear profile (11.5 ± 2.8, 11.4 ± 3.6) and roughness (2.6 ± 0.3, 3.3 ± 0.3), respectively. In images, we observed that gHCl could cause enamel erosion in both groups. Conclusion: Gaseous hydrochloric acid causes similar enamel erosion on bovine and humans

Laser managed in the treatment of hypomineralized occlusal defects in teeth enamel affected by molar-incisor hypomineralization: A randomized controlled clinical study / Uso do laser no tratamento dos defeitos oclusais hipomineralizados em esmalte de dentes afetados pela hipomineralização molar-incisivo: estudo clínico controlado randomizado

Background: Nowadays, observed a growing rate of teeth affected by molar incisor hypomineralization (MIH). These teeth can present persistent inflammation of the pulp, increasing the dentin hypersensitivity and consequently, directly affecting the cleaning of the affected tooth and contributing to the progression of caries lesions. Aims: This study aims to compare the use of diode laser (DL) irradiation (970nm) with the application of a glass ionomer-based sealant (GIC) for the most clinically and cost-effective strategy for the management of first permanent molars affected with MIH. Methods: This is a two-arm, parallel-group, patient randomized superiority-controlled trial, children present MIH molars will be selected and treated either with the application of DL or with the application of GIC-based sealants. Baseline and follow-up evaluations will be assessed through clinical examination and analysis of dental impressions that will be carried out of the affected teeth. The outcomes evaluated will be: 1) presence of post-eruptive breakdown and/or atypical dentin caries lesions, 2) retention rate of sealants 3) parent’s satisfaction, 4) children’s hypersensitivity 5) child-self-reported discomfort 6) impact on the quality of life and 7) the incremental cost-effectiveness. Evaluations will be performed by one trained evaluator after one week, and 1, 6, 12, 18, and 24 months. Multilevel statistical analyzes will be conducted to establish the ability of DL treatment compared to sealing, in joining to plausible factors associated with this efficacy. Discussion: We expect that this study contributes to the best scientific proof concerning the most cost-effective treatment for permanent molars affected with MIH

Microhardness of composite resins at different depths varying the post-irradiation time

OBJECTIVE: The purpose of this study was to assess the microhardness of posterior composite resins at different depths varying the post-irradiation time. MATERIALS AND METHODS: For each composite resin [Solitaire 2 (SO) - Heraus Kulzer, P60 (P) - 3M, Prodigy Condesable (PC) - Kerr, Surefil (S) - Dentsply and Alert (A) - Pentron], 6 specimens (3 mm in diameter; 4mm high) were prepared using a black polyurethane cylindrical matrix. The resins were inserted in a bulk increment and light cured for 40 seconds. Microhardness was analyzed at different depths (top, 0.4 mm, 1.0 mm, 2.0mm, 3.0 mm and 4.0 mm) and at two moments (20 minutes and 24 hours after light-curing). Data were analyzed by ANOVA and Tukey's test (

Effect of Nd:YAG laser combined with fluoride on the prevention of primary tooth enamel demineralization

Most studies dealing with the caries preventive action of Nd:YAG laser have been done in permanent teeth and studies on primary teeth are still lacking. The aim of this study was to evaluate in vitro the effect of Nd:YAG laser combined or not with fluoride sources on the acid resistance of primary tooth enamel after artificial caries induction by assessing longitudinal microhardness and demineralization depth. Sixty enamel blocks obtained from the buccal/lingual surface of exfoliated human primary molars were coated with nail polish/wax, leaving only a 9 mm² area exposed on the outer enamel surface, and randomly assigned to 6 groups (n=10) according to the type of treatment: C-control (no treatment); APF: 1.23% acidulated phosphate fluoride gel; FV: 5% fluoride varnish; L: Nd:YAG laser 0.5 W/10 Hz in contact mode; APFL: fluoride gel + laser; FVL: fluoride varnish + laser. After treatment, the specimens were subjected to a des-remineralization cycle for induction of artificial caries lesions. Longitudinal microhardness data (%LMC) were analyzed by the Kruskal-Wallis test and demineralization depth data were analyzed by oneway ANOVA and Fisher&#8217;s LSD test (á=0.05). APFL and APF groups presented the lowest percentage of microhardness change (p<0.05). Demineralization depth was smaller in all treated groups compared with the untreated control. In conclusion, Nd:YAG laser combined or not with fluoride gel/varnish was not more effective than fluoride alone to prevent enamel demineralization within the experimental period

Effectiveness of home bleaching agents in discolored teeth and influence on enamel microhardness

OBJECTIVES: This study evaluated the effectiveness of different home bleaching agents on color alteration and their influence on surface and subsurface microhardness of discolored bovine enamel. MATERIAL AND METHODS: Forty-five fragments of bovine incisors were randomly allocated into 3 groups (n=15) according to the bleaching agent: 10% carbamide peroxide gel (CP10), 16% carbamide peroxide gel (CP16) and 6.5%-hydrogen-peroxide-based strip (HP6.5). Before bleaching treatment, initial values of Knoop surface microhardness and color (CIEL*a*b*) were obtained and the fragments were artificially stained in hemolyzed rat blood. Then, bleaching treatments were performed over a 21-day period. Color changes (&#916;E) were assessed at 7, 14 and 21 days, and final surface microhardness reading was done after 21 days. Thereafter, the fragments were bisected to obtain subsurface microhardness. Data were subjected to ANOVA and Tukey's tests (&#945;=5%). RESULTS: Color changes produced by CP16 were similar to those of CP10, and the color changes produced by these materials were significantly superior to those produced by HP6.5. Color changes at 21 days were superior to 7 days and similar to 14 days. The time did not influence color changes for CP16, which showed similarity between the 14- and 21-day results. No statistically significant differences were found among the home bleaching agents for surface and subsurface microhardness. CONCLUSIONS: Microhardness of bovine enamel was not affected by the bleaching agents. The 16% carbamide peroxide gel was the most effective for bleaching the stained substrate

Composite resin color stability: influence of light sources and immersion media

OBJECTIVE: This study evaluated the influence of light sources and immersion media on the color stability of a nanofilled composite resin. MATERIAL AND METHODS: Conventional halogen, high-power-density halogen and high-power-density light-emitting diode (LED) units were used. There were 4 immersion media: coffee, tea, Coke® and artificial saliva. A total of 180 specimens (10 mm x 2 mm) were prepared, immersed in artificial saliva for 24 h at 37±1ºC, and had their initial color measured with a spectrophotometer according to the CIELab system. Then, the specimens were immersed in the 4 media during 60 days. Data from the color change and luminosity were collected and subjected to statistical analysis by the Kruskall-Wallis test (

Effect of diode laser irradiation on the bond strength of polymerized nonsimplified adhesive systems after 12 months of water storage

Objectives: The aim of this in vitro study was to evaluate the bonding strength of non-simplified dentin bonding systems (DBS) to dentin irradiated with a diode laser (970 nm) immediately and after 12 months of water storage following either primer or bond application. Material and methods: The experimental design included three different factors: DBS type [AdperTM Scotchbond Multipurpose (MP) and ClearfilTM SE Bond (CSE)], irradiation [without irradiation - control (C), irradiation after primer application (AP), and irradiation after bond application (AB)], and time [initial (I) and after 12 months of water storage (12 m)]. Sixty sound human third molars (n=10) were obtained, and their flat occlusal dentin areas were prepared and standardized. Laser irradiation was performed in the contact mode perpendicular to the dental surface over an automatically selected scanning area at a pulse energy of 0.8 W, frequency of 10 Hz, and energy density of 66.67 J/cm2. After 7 days of treatment, the specimens were cut, and half of them were subjected to microtensile testing (500 N/0.05 mm/min), whereas the remaining sticks were examined after 12 months of water storage. The obtained data were analyzed by three-way analysis of variance (ANOVA) followed by a Tukey test (p&lt;0.05). The observed fracture modes were investigated using a portable digital microscope with a magnification of 40x. Results: Among the utilized DBS, MP generally exhibited higher bond strengths, but did not always differ from CSE under similar conditions. The irradiation factor was statistically significant only for the MP/AB groups. After 12 months of storage, all groups demonstrated a significant reduction in the bond strength, whereas the results of fracture analysis showed a predominance of the adhesive type. Conclusions: The laser treatment of non-simplified DBS was not able to stabilize their bonding characteristics after 12 months

Effect of diode laser irradiation on the bond strength of polymerized nonsimplified adhesive systems after 12 months of water storage

Objectives: The aim of this in vitro study was to evaluate the bonding strength of non-simplified dentin bonding systems (DBS) to dentin irradiated with a diode laser (970 nm) immediately and after 12 months of water storage following either primer or bond application. Material and methods: The experimental design included three different factors: DBS type [AdperTM Scotchbond Multipurpose (MP) and ClearfilTM SE Bond (CSE)], irradiation [without irradiation - control (C), irradiation after primer application (AP), and irradiation after bond application (AB)], and time [initial (I) and after 12 months of water storage (12 m)]. Sixty sound human third molars (n=10) were obtained, and their flat occlusal dentin areas were prepared and standardized. Laser irradiation was performed in the contact mode perpendicular to the dental surface over an automatically selected scanning area at a pulse energy of 0.8 W, frequency of 10 Hz, and energy density of 66.67 J/cm2. After 7 days of treatment, the specimens were cut, and half of them were subjected to microtensile testing (500 N/0.05 mm/min), whereas the remaining sticks were examined after 12 months of water storage. The obtained data were analyzed by three-way analysis of variance (ANOVA) followed by a Tukey test (p&lt;0.05). The observed fracture modes were investigated using a portable digital microscope with a magnification of 40x. Results: Among the utilized DBS, MP generally exhibited higher bond strengths, but did not always differ from CSE under similar conditions. The irradiation factor was statistically significant only for the MP/AB groups. After 12 months of storage, all groups demonstrated a significant reduction in the bond strength, whereas the results of fracture analysis showed a predominance of the adhesive type. Conclusions: The laser treatment of non-simplified DBS was not able to stabilize their bonding characteristics after 12 months