A study on corrosion resistance of ISO 5832-1 austenitic stainless steel used as orthopedic implant

The ISO 5832-1 austenitic stainless steel used as biomaterial is largely applied in the area of orthopedics, especially in the manufacture of implants, such as temporary or permanent replacement of bone structures. The objective of this study was to evaluate the localized corrosion resistance of the ISO 5832-1 stainless steel used in orthopedic implants by electrochemical tests in two different solutions. The results of this study are of great interest to evaluate the corrosion of metallic implants that can result in the release of corrosion products into bodily fluids causing possible adverse biological reactions. The determination of the chemical elements in the composition of the ISO 5832-1 stainless steel was performed by neutron activation analysis (NAA). The samples for electrochemical tests were grinded with silicon carbide paper up to #4000 finishing, followed by mechanical polishing with diamond paste. The open circuit potential measurements and anodic polarization curves were obtained in solution of 0.90 wt. % of NaCl and of simulated body fluid (SBF). The results indicated that the ISO 5832-1 stainless steel presented a high resistance to crevice corrosion in simulated body fluid solution but high susceptibility to this form of corrosion in the chloride solution. &nbsp

Study of ph effect on AZ31 magnesium alloy corrosion for using in temporary implants

Currently, magnesium alloys are gaining great interest for medical applications due to their degrading properties in the human body ensuring a great biocompatibility. These alloys also provide profitable mechanical properties due similarities with human bone.  However, a difficulty in applying these materials in the biomaterials industries is the corrosion prior to cell healing. The effect of the chemical composition of Mg alloys on their corrosion behavior is well known. In this study, samples of AZ31 magnesium alloy were cut into chips for elemental chemical analysis by neutron activation analysis (NAA). Concentrations of the elements As, La, Mg, Mn, Na, Sb and Zn were determined in the AZ31 alloy. Visualization tests of agar corrosion development in various media, of 0.90% sodium chloride solution (mass), phosphate buffer saline (PBS) and simulated body fluid (SBF) were performed. Visualizations of the effect of agar gel corrosion revealed pH variation during the corrosion process due to the released into the cathode. The highest released of hydroxyl ions occurred in NaCl solution compared to PBS and SBF solutions indicating that NaCl solution was much more aggressive to the alloy compared to the others

Determinants of corrosion resistance of Ti-6Al-4V alloy dental implants in an In Vitro model of peri-implant inflammation.

BACKGROUND:Titanium (Ti) and its alloys possess high biocompatibility and corrosion resistance due to Ti ability to form a passive oxide film, i.e. TiO2, immediately after contact with oxygen. This passive layer is considered stable during function in the oral cavity, however, emerging information associate inflammatory peri-implantitis to vast increases in Ti corrosion products around diseased implants as compared to healthy ones. Thus, it is imperative to identify which factors in the peri-implant micro-environment may reduce Ti corrosion resistance. METHODS:The aim of this work is to simulate peri-implant inflammatory conditions in vitro to determine which factors affect corrosion susceptibility of Ti-6Al-4V dental implants. The effects of hydrogen peroxide (surrogate for reactive oxygen species, ROS, found during inflammation), albumin (a protein typical of physiological fluids), deaeration (to simulate reduced pO2 conditions during inflammation), in an acidic environment (pH 3), which is typical of inflammation condition, were investigated. Corrosion resistance of Ti-6Al-4V clinically-relevant acid etched surfaces was investigated by electrochemical techniques: Open Circuit Potential; Electrochemical Impedance Spectroscopy; and Anodic Polarization. RESULTS:Electrochemical tests confirmed that most aggressive conditions to the Ti-6Al-4V alloy were those typical of occluded cells, i.e. oxidizing conditions (H2O2), in the presence of protein and deaeration of the physiological medium. CONCLUSIONS:Our results provide evidence that titanium's corrosion resistance can be reduced by intense inflammatory conditions. This observation indicates that the micro-environment to which the implant is exposed during peri-implant inflammation is highly aggressive and may lead to TiO2 passive layer attack. Further investigation of the effect of these aggressive conditions on titanium dissolution is warranted