Ferroelectric properties of (1 − x)Bi(Zn1/2Ti1/2)O3–xPbZrO3 ceramics

The (1 − x)Bi(Zn1/2Ti1/2)O3–xPbZrO3 solid solution ceramics were prepared by using solid-state reaction method, and their ferroelectric properties were investigated. It was found that the perovskite structure is stable for compositions with x ≥ 0.900. Within this composition range, the crystal structure of the solid solution preserves the orthorhombic symmetry of PbZrO3 (PZ). The Curie point of the ceramics was found to decrease with increasing Bi(Zn1/2Ti1/2)O3 (BZT) content. The intermediate ferroelectric phase of PZ was stabilized by BZT addition and exists within a much wider temperature range in the solid solution

The morphotropic phase boundary and electrical properties of (1 − x)Pb(Zn1/2W1/2)O3–xPb(Zr0.5Ti0.5)O3 ceramics

Ceramics in the solid solution of (1 − x)Pb(Zn1/2W1/2)O3–xPb(Zr0.5Ti0.5)O3 system, with x = 0.80, 0.85, 0.90, and 0.95, were synthesized with the solid-state reaction technique. The perovskite phase formation in the sintered ceramics was analyzed with X-ray diffraction. It shows that the rhombohedral and the tetragonal phases coexist in the ceramic with x = 0.90, indicating the morphotropic phase boundary (MPB) within this pseudo-binary system. Dielectric and ferroelectric properties measurements indicate that the transition temperature decreases while the remanent polarization increases with the addition of Pb(Zn1/2W1/2)O3. In the composition of x = 0.85 which is close to the MPB in the rhombohedral side, a high piezoelectric property with d 33 = 222 pC/N was observed

Acoustic emission and dielectric studies of phase transitions within the morphotropic phase boundary of xPb(Zr1/2Ti1/2)O3-(1−x)Pb(Ni1/3Nb2/3)O3 relaxor ferroelectrics

We have carried out a combined acoustic emission(AE) and dielectricpermittivity study of the xPb(Zr1/2Ti1/2)O3-(1−x)Pb(Ni1/3Nb2/3)O3relaxor ferroelectric ceramics with compositions x=0.7–0.9 corresponding to its morphotropic phase boundary. Temperatures of all phase transitions occurring on heating are identified accurately by AE, and a direct transition between the low-temperature (rhombohedral) and high-temperature (pseudocubic) relaxor phases is found. The AE peak intensity is generally proportional to the temperature derivative of the dielectricpermittivity, in agreement with a model proposed for a thermally cycled small elastic dipole

Ferroelectric properties of (1 − x)Bi(Zn1/2Ti1/2)O3–xPbZrO3 ceramics

The (1 − x)Bi(Zn1/2Ti1/2)O3–xPbZrO3 solid solution ceramics were prepared by using solid-state reaction method, and their ferroelectric properties were investigated. It was found that the perovskite structure is stable for compositions with x ≥ 0.900. Within this composition range, the crystal structure of the solid solution preserves the orthorhombic symmetry of PbZrO3 (PZ). The Curie point of the ceramics was found to decrease with increasing Bi(Zn1/2Ti1/2)O3 (BZT) content. The intermediate ferroelectric phase of PZ was stabilized by BZT addition and exists within a much wider temperature range in the solid solution.This is a manuscript from Journal of Materials Science 44 (2009): 4321, doi: 10.1007/s10853-009-3644-z. The final publication is available at Springer via http://dx.doi.org/doi:10.1007/s10853-009-3644-z.</p

The morphotropic phase boundary and electrical properties of (1 − x)Pb(Zn1/2W1/2)O3–xPb(Zr0.5Ti0.5)O3 ceramics

Ceramics in the solid solution of (1 − x)Pb(Zn1/2W1/2)O3–xPb(Zr0.5Ti0.5)O3 system, with x = 0.80, 0.85, 0.90, and 0.95, were synthesized with the solid-state reaction technique. The perovskite phase formation in the sintered ceramics was analyzed with X-ray diffraction. It shows that the rhombohedral and the tetragonal phases coexist in the ceramic with x = 0.90, indicating the morphotropic phase boundary (MPB) within this pseudo-binary system. Dielectric and ferroelectric properties measurements indicate that the transition temperature decreases while the remanent polarization increases with the addition of Pb(Zn1/2W1/2)O3. In the composition of x = 0.85 which is close to the MPB in the rhombohedral side, a high piezoelectric property with d 33 = 222 pC/N was observed.This is a manuscript of an article from Journal of Materials Science 44 (2009): 1868, doi:10.1007/s10853-008-3235-4. The final publication is available at Springer via http://dx.doi.org/10.1007/s10853-008-3235-4.</p

Acoustic emission and dielectric studies of phase transitions within the morphotropic phase boundary of xPb(Zr1/2Ti1/2)O3-(1−x)Pb(Ni1/3Nb2/3)O3 relaxor ferroelectrics

We have carried out a combined acoustic emission(AE) and dielectricpermittivity study of the xPb(Zr1/2Ti1/2)O3-(1−x)Pb(Ni1/3Nb2/3)O3relaxor ferroelectric ceramics with compositions x=0.7–0.9 corresponding to its morphotropic phase boundary. Temperatures of all phase transitions occurring on heating are identified accurately by AE, and a direct transition between the low-temperature (rhombohedral) and high-temperature (pseudocubic) relaxor phases is found. The AE peak intensity is generally proportional to the temperature derivative of the dielectricpermittivity, in agreement with a model proposed for a thermally cycled small elastic dipole.The following article appeared in Applied Physics Letters 95 (2009): 252903, and may be found at http://dx.doi.org/10.1063/1.3275730.</p