Surface degradation of glass ceramics after exposure to acidulated phosphate fluoride

OBJECTIVE: This study evaluated the surface degradation effect of acidulated phosphate fluoride (APF) gel exposure on the glassy matrix ceramics as a function of time. MATERIAL AND METHODS: Disc-shaped ceramic specimens (N = 120, 10/per ceramic material) were prepared in stainless steel molds (inner diameter: 5 mm, height: 2 mm) using 6 dental ceramics: 3 indicated for ceramic-fused-to-metal (Vita Omega 900, Carmen and Vita Titankeramik), 2 for all-ceramic (Vitadur Alpha and Finesse® Low Fusing) and 1 for both types of restorations (IPS d.SIGN). The specimens were wet ground finished, ultrasonically cleaned and auto-glazed. All specimens were subjected to calculation of percentage of mass loss, surface roughness analysis and topographical description by scanning electron microscopy (SEM) before (0 min) and after exposure to 1.23 % APF gel for 4 min and 60 min representing short- and long-term etching effect, respectively. The data were analyzed using two-way ANOVA with repeated measures and Tukey's test (a=0.05). RESULTS: Significant effect of the type of the ceramics (p=0.0000, p=0.0031) and exposure time (p=0.0000) was observed in both surface roughness and percentage of mass loss values, respectively. The interaction factor between both parameters was also significant for both parameters (p=0.0904, p=0.0258). Both 4 min (0.44±0.1 - 0.81±0.2 mm) and 60 min (0.66±0.1 - 1.04±0.3 mm) APF gel exposure created significantly more surface roughness for all groups when compared to the control groups (0.33±0.2 - 0.68±0.2 mm) (p;0.05) but at 60 min exposure, IPS d.SIGN showed the highest percentage of mass loss (0.1151±0.11). The mean surface roughness for Vita Titankeramik (0.84±0.2 mm) and Finesse® Low Fusing (0.74.±0.2 mm) was significantly higher than those of the other ceramics (0.59±0.1 mm - 0.49±0.1 mm) and Vita Titankeramik (

Machined and plastic copings in three-element prostheses with different types of implantabutment joints: a strain gauge comparative analysis

OBJECTIVE: Using strain gauge (SG) analysis, the aim of this in vitro study was quantify the strain development during the fixation of three-unit screw implant-supported fixed partial dentures, varying the types of implant-abutment joints and the type of prosthetic coping. The hypotheses were that the type of hexagonal connection would generate different microstrains and the type of copings would produce similar microstrains after prosthetic screws had been tightened onto microunit abutments. MATERIALS AND METHODS: Three dental implants with external (EH) and internal (IH) hexagonal configurations were inserted into two polyurethane blocks. Microunit abutments were screwed onto their respective implant groups, applying a torque of 20 Ncm. Machined Co-Cr copings (M) and plastic prosthetic copings (P) were screwed onto the abutments, which received standard wax patterns. The wax patterns were cast in Co-Cr alloy (n=5), forming four groups: G1) EH/M; G2) EH/P; G3) IH/M and G4) IH/P. Four SGs were bonded onto the surface of the block tangentially to the implants, SG 1 mesially to implant 1, SG 2 and SG 3 mesially and distally to implant 2, respectively, and SG 4 distally to implant 3. The superstructure's occlusal screws were tightened onto microunit abutments with 10 Ncm torque using a manual torque driver. The magnitude of microstrain on each SG was recorded in units of microstrain (µε). The data were analyzed statistically by ANOVA and Tukey's test (p0.05). The hypotheses were partially accepted. CONCLUSIONS: It was concluded that the type of hexagonal connection and coping presented similar mechanical behavior under tightening conditions

2 nd Brazilian Consensus on Chagas Disease, 2015

Abstract Chagas disease is a neglected chronic condition with a high burden of morbidity and mortality. It has considerable psychological, social, and economic impacts. The disease represents a significant public health issue in Brazil, with different regional patterns. This document presents the evidence that resulted in the Brazilian Consensus on Chagas Disease. The objective was to review and standardize strategies for diagnosis, treatment, prevention, and control of Chagas disease in the country, based on the available scientific evidence. The consensus is based on the articulation and strategic contribution of renowned Brazilian experts with knowledge and experience on various aspects of the disease. It is the result of a close collaboration between the Brazilian Society of Tropical Medicine and the Ministry of Health. It is hoped that this document will strengthen the development of integrated actions against Chagas disease in the country, focusing on epidemiology, management, comprehensive care (including families and communities), communication, information, education, and research

Effect of Thermocycling on the Bond Strength Between a Pure Commercially Titanium and Ceromer

Objective: To verify, using a shear mechanic test, the effect of the thermocycling on the bond strength between a pure commercially titanium (cpTi) and the esthetic veneer material (Resilab Wilcos/Brazil). Method: Twenty metallic cylinders (n=20), with 5mm of length and 4mm of diameter each one were obtained by machining of titanium bars. The metallic bars were sandblasted with aluminum oxide (250µm), at 2 bars of pressure for 20 seconds, with 3cm of distance. After was applied the adhesive system of the veneer material, Resibond (Wilcos/Brazil), and later the opaque Resilab and veneer on the metallic bases. The samples were stored in distilled water for 24 hours, at 37ºC and after randomly divided into 2 groups: G1 (control) and G2 (experimental), which was submitted to 500 thermocycles (5º/55ºC±1, dwell time: 30 s). The two groups were submitted to shear test in a universal testing machine (model DL-1000, EMIC Equipments and Systems Ltda., Sao Jose dos Pinhais - PR - Brazil) with a 500kg load cell at a speed of 0.5mm/min. The numeric dates (MPa) were submitted to the Mann-Whitney test (p=0.038). Results: After the dates analysis, was observed that the group G1 (7.83-18.72) was statistically different from the group G2 (5.51-15.34). Conclusion: Based on the results is lawful conclude that there was a significance reduction on the bond strength after thermocycling

Histometric analysis and topographic characterization of cp Ti implants with surfaces modified by laser with and without silica deposition

Biologic behavior of the bone tissue around implants with four different surfaces was evaluated. The surfaces were: modified by laser (LS); modified by laser with sodium silicate deposition (SS); and commercially available surfaces modified by acid etching (AS) and machined surface (MS). Topographic characterization of the surfaces was performed by scanning electron microscopy (SEM)- energy dispersive X-ray spectrometry (EDX) before experimental surgery. Thirty rabbits received 60 implants in their right and left tibias, 1 implant of each surface being placed in each tibia. The analyzed periods were 4,8, and 12 weeks postoperatively. Histometric analysis was performed evaluating bone interface contact (SIC) and bone area (BA). The results obtained were submitted to the analysis of variance and the Tukey t-test. The elemental mapping was evaluated by means of SEM at 4 weeks postoperatively. The topographic characterization showed differences between the analyzed surfaces. Generally, the BIC and BA of LS and SS implants were statistically higher than those of AS and MS in most of the analyzed periods. Elemental mapping showed high peaks of calcium and phosphorous in all groups. Based on the present methodology, it may be concluded that experimental modifications LS and SS accelerated the stages of the bone tissue repair process around the implants, providing the highest degree of osseointegration. (C) 2014 Wiley Periodicals, Inc.Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP