2 research outputs found
The in vitro and in vivo capacity of culture-expanded human cells from several sources encapsulated in alginate to form cartilage
Abstract
Cartilage has limited self-regenerative capacity. Tissue engineering can offer promising solutions for reconstruction of missing or damaged cartilage. A major challenge herein is to define an appropriate cell source that is capable of generating a stable and functional matrix. This study evaluated the performance of culture-expanded human chondrocytes from ear (EC), nose (NC) and articular joint (AC), as well as bone-marrow-derived and adipose-tissue-derived mesenchymal stem cells both in vitro and in vivo. All cells (≥ 3 donors per source) were culture-expanded, encapsulated in alginate and cultured for 5 weeks. Subsequently, constructs were implanted subcutaneously for 8 additional weeks. Before and after implantation, glycosaminoglycan (GAG) and collagen content were measured using biochemical assays. Mechanical properties were determined using stress-strain-indentation tests. Hypertrophic differentiation was evaluated with qRT-PCR and subsequent endochondral ossification with histology. ACs had higher chondrogenic potential in vitro than the other cell sources, as assessed by gene expression and GAG content (p < 0.001). However, after implantation, ACs did not further increase their matrix. In contrast, ECs and NCs continued producing matrix in vivo leading to higher GAG content (p < 0.001) and elastic modulus. For NC-constructs, matrix-deposition was associated with the elastic modulus (R² = 0.477, p = 0.039). Although all cells--except ACs--expressed markers for hypertrophic differentiation in vitro, there was no bone formed in vivo. Our work shows that cartilage formation and functionality depends on the cell source used. ACs possess the highest chondrogenic capacity in vitro, while ECs and NCs are most potent in vivo, making them attractive cell sources for cartilage repair
Mechanical and biochemical mapping of human auricular cartilage for reliable assessment of tissue-engineered constructs
It is key for successful auricular (AUR) cartilage tissue-engineering (TE) to ensure that the engineered cartilage mimics the mechanics of the native tissue. This study provides a spatial map of the mechanical and biochemical properties of human auricular cartilage, thus establishing a benchmark for the evaluation of functional competency in AUR cartilage TE. Stress-relaxation indentation (instantaneous modulus, Ein; maximum stress, σmax; equilibrium modulus, Eeq; relaxation half-life time, t1/2; thickness, h) and biochemical parameters (content of DNA; sulfated-glycosaminoglycan, sGAG; hydroxyproline, HYP; elastin, ELN) of fresh human AUR cartilage were evaluated. Samples were categorized into age groups and according to their harvesting region in the human auricle (for AUR cartilage only). AUR cartilage displayed significantly lower Ein, σmax, Eeq, sGAG content; and significantly higher t1/2, and DNA content than NAS cartilage. Large amounts of ELN were measured in AUR cartilage (>15% ELN content per sample wet mass). No effect of gender was observed for either auricular or nasoseptal samples. For auricular samples, significant differences between age groups for h, sGAG and HYP, and significant regional variations for Ein, σmax, Eeq, t1/2, h, DNA and sGAG were measured. However, only low correlations between mechanical and biochemical parameters were seen (R<0.44). In conclusion, this study established the first comprehensive mechanical and biochemical map of human auricular cartilage. Regional variations in mechanical and biochemical properties were demonstrated in the auricle. This finding highlights the importance of focusing future research on efforts to produce cartilage grafts with spatially tunable mechanics