14 research outputs found
Tris(tert-butyl 3-oxobutanoato-kappa O-2(1),O- )-aluminium(III) at 153 K
In the title complex, [Al(C8H13O3)(3)], a potential metal-organic chemical vapour deposition (MOCVD) precursor, three bidentate ligand molecules are bound to the metal atom, forming an octahedral geometry. Two non-planar six-membered chelate rings adopt screw-boat conformations, while the third ring has a conformation that lies about halfway between an envelope and a screw-boat
Nanocrystalline TiO(2) preparation by microwave route and nature of anatase-rutile phase transition in nano TiO(2)
Nanopowders of TiO(2) has been prepared using a microwave irradiation-assisted route, starting from a metalorganic precursor, bis(ethyl-3-oxo-butanoato)oxotitanium (IV), [TiO(etob)(2)](2). Polyvinylpyrrolidone (PVP) was used as a capping agent. The as-prepared amorphous powders crystallize into anatase phase, when calcined. At higher calcination temperature, the rutile phase is observed to form in increasing quantities as the calcination temperature is raised. The structural and physicochemical properties were measured using XRD, FT-IR, SEM, TEM and thermal analyses. The mechanisms of formation of nano-TiO(2) from the metal-organic precursor and the irreversible phase transformation of nano TiO(2) from anatase to rutile structure at higher temperatures have been discussed. It is suggested that a unique step of initiation of transformation takes place in Ti(1/2)O layers in anatase which propagates. This mechanism rationalizes several key observations associated with the anatase rutile transformation