2 research outputs found

    Synthesis, Structure, and Properties of EuLnCuSe<sub>3</sub> (Ln = Nd, Sm, Gd, Er)

    No full text
    EuLnCuSe3 (Ln = Nd, Sm, Gd, Er), due to their complex composition, should be considered new materials with the ability to purposefully change the properties. Samples of the EuLnCuSe3 were prepared using Cu, rare earth metal, Se (99.99%) by the ampoule method. The samples were obtained by the crystallization from a melt and annealed at temperatures 1073 and 1273 K. The EuErCuSe3 crystal structure was established using the single-crystal particle. EuErCuSe3 crystallizes in the orthorhombic system, space group Cmcm, KCuZrS3 structure type, with cell parameters a = 4.0555 (3), b = 13.3570 (9), and c = 10.4602 (7) Å, V = 566.62 (6) Å3. In structure EuErCuSe3, erbium ions are coordinated by selenium ions in the octahedral polyhedron, copper ions are in the tetrahedral coordination, europium ions are between copper and erbium polyhedra layers and are coordinated by selenium ions as two-cap trigonal prisms. The optical band gap is 1.79 eV. At 4.7 K, a transition from the ferrimagnetic state to the paramagnetic state was detected in EuErCuSe3. At 85 and 293 K, the compound is in a paramagnetic state. According to XRPD data, EuLnCuSe3 (Ln = Nd, Sm, Gd) compounds have a Pnma orthorhombic space group of the Eu2CuS3 structure type. For EuSmCuSe3, a = 10.75704 (15) Å, b = 4.11120 (5) Å, c = 13.37778 (22) Å. In the series of EuLnCuSe3 compounds, the optical band gap increases 1.58 eV (Nd), 1.58 eV (Sm), 1.72 eV (Gd), 1.79 eV (Er), the microhardness of the 205 (Nd), 210 (Sm), 225 (Gd) 235 ± 4 HV (Er) phases increases, and the thermal stability of the phases increases significantly. According to the measurement data of differential scanning calorimetry, the EuNdCuSe3 decomposes, according to the solid-phase reaction T = 1296 K, ΔH = 8.2 ± 0.8 kJ/mol. EuSmCuSe3 melts incongruently T = 1449 K, ΔH = 18.8 ± 1.9 kJ/mol. For the EuGdCuSe3, two (Tα↔β = 1494 K, ΔHα↔β = 14.8 kJ/mol, Tβ↔γ = 1530 K, ΔHβ↔γ = 4.8 kJ/mol) and for EuErCuSe3 three polymorphic transitions (Tα↔β = 1561 K, ΔHα↔β = 30.3 kJ/mol, Tβ↔γ = 1579 K, ΔHβ↔γ = 4.4 kJ/mol, and Tγ↔δ = 1600 K, ΔHγ↔δ = 10.1 kJ/mol). The compounds melt incongruently at the temperature of 1588 K, ΔHmelt = 17.9 ± 1.8 kJ/mol and 1664 K, ΔHmelt = 25.6 ± 2.5 kJ/mol, respectively. Incongruent melting of the phases proceeds with the formation of a solid solution of EuSe and a liquid phase

    Magnetic, Optical, and Thermic Properties of SrLnCuSe<sub>3</sub> (Ln = Dy, Ho, Er, Tm) Compounds

    No full text
    SrLnCuSe3 (Ln = Dy, Ho, Er, Tm) compounds crystallize in the Pnma and Cmcm orthorhombic space group and belong to the Eu2CuS3 and KCuZrS3 structural type, respectively. According to a single-crystal XRD study, the SrTmCuSe3 unit cell parameters are a = 4.0631 (4), b = 13.4544 (14), c = 10.4430 (10) Å, and V = 570.88 (10) Å3. All the studied SrLnCuSe3 samples in the temperature range of 1.77–300 K demonstrate paramagnetic behavior without any features pointing to magnetic ordering. The measured Curie constants coincide with the values expected for Ln3+ ions with good accuracy, which confirms the stoichiometric composition of the samples and the non-magnetic state of the copper ions, Cu1+ (S = 0). The conducted optical absorption study showed that the polycrystalline SrLnCuSe3 (Ln = Dy, Ho, Er, Tm) samples are semiconductors with a direct bandgap ranging from 2.14 eV to 2.31 eV. Two indirect bandgaps were revealed and explained by the presence of optical transitions to highly dispersive subbands in the conduction band. The compounds demonstrate two reversible phase transitions α⇆β, β⇆γ and an incongruent melting at 1606 K (Dy), 1584 K (Ho), 1634 K (Er), and 1620 K (Tm) associated with the formation of solid solutions of SrSe, Cu2-XSe, and Ln2Se3 binary compounds
    corecore