Comparison of the shear bond strength of self-adhesive resin cements to enamel and dentin with different protocol of application

Aim: The aim of the present study was to determine the shear bond strength of self-adhesive resin cements to enamel and dentin with and without surface treatments, and compare them with conventional resin cement as the control group. Methods: In this experimental study, buccal and lingual surface of the thirty sound human premolars were polished in order to obtain a flat surface of enamel (E) in buccal, and dentin (D) in lingual. Sixty feldspathic ceramic blocks (2×3×3 mm) were prepared and randomly divided into six groups (n=10). Each block was cemented to the prepared surface (30 enamel and 30 dentin surface) according to different protocol: E1 and D1; RelyX ARC as control group, E2, D2; RelyX Unicem, E3, D3; acid etching +RelyX Unicem. The specimens were termocycled and subjected to shear forces by a universal testing machine at a cross head speed of 0.5 mm/min. The mode of fracture were evaluated by stereomicroscope. Data were analyzed with descriptive statistical methods using SPSS version 15. One-way ANOVA, and post hoc Tukey tests were used to compare bond strengths between the groups with different adhesives at α=0.05. Results: Statistical analysis showed no significant differences within the enamel subgroups, but there were significant differences within the dentinal subgroups, and statistically significant differences were found between the groups D1and D3 (p=0.02). Comparison between similar enamel and dentinal subgroups showed that there was a significant difference just between the subgroups E3 and D3 (p=0.01). Conclusion: Elective etching of enamel did not lead to significant increase in the shear bond strength of RelyX Unicem in comparison to RelyX ARC. On the other hand, elective etching of dentin reduces the bond strength of RelyX Unicem with the dentin

Effect of hydrophobic resin following different dentin bondings application on nanoleakage of composite restorations

Background and Aims: The aim of the present study was to evaluate the effect of applying hydrophobic resin after use of different generation of the bonding systems on nanoleakage. Materials and Methods: 20 third molar teeth were selected. The teeth were randomly divided into 4 groups of 5, each was treated using the fourth, fifth, sixth, and seven generation of dentin bonding. Then, the crown of teeth was sectioned from the CEJ region and each specimen was divided into two halves with mesiodistal cut, one half for the application of dentin bonding without the addition of a hydrophobic resin, and the other for the same dentin bonding by the addition of a hydrophobic resin. Afterwards, the specimens were restotred by composites. After placement of specimens in silver nitrate, the amount of nanoleakage was evaluated by SEM. Data were analyzed using a repeated measurement statistical analysis (α=0.05). Results: The use of hydrophobic resins decreased nanoleakage and range of variations in all groups (P<0.05). This reduction was greater for total-etch dentin bonding. Higher degree of nanoleakage occurred in total-etch dentin bonding in most evaluated areas. In general, Clearfil S³ bond showed the least percent of the nanoleakage. Conclusion: All dentin bonding systems showed some degree of reduction in nanoleakage after hydrophobic layer application and the reduction was greater in Total-etch adhesives systems