The Effect of Exposed Glass Fibers and Particles of Bioactive Glass on the Surface Wettability of Composite Implants
Measurement of the wettability of a material is a predictive index of cytocompatibility. This study was designed to evaluate the effect of exposed E-glass fibers and bioactive glass (BAG) particles on the surface wettability behavior of composite implants. Two different groups were investigated: (a) fiber reinforced composites (FRCs) with different fiber orientations and (b) polymer composites with different wt. % of BAG particles. Photopolymerized and heat postpolymerized composite substrates were made for both groups. The surface wettability, topography, and roughness were analyzed. Equilibrium contact angles were measured using the sessile drop method. Three liquids were used as a probe for surface free energy (SFE) calculations. SFE values were calculated from contact angles obtained on smooth surfaces. The surface with transverse distribution of fibers showed higher (P < 0.001) polar (γP) and total SFE (γTOT) components (16.9 and 51.04 mJ/m2, resp.) than the surface with in-plane distribution of fibers (13.77 and 48.27 mJ/m2, resp.). The increase in BAG particle wt. % increased the polar (γP) value, while the dispersive (γD) value decreased. Postpolymerization by heat treatment improved the SFE components on all the surfaces investigated (P < 0.001). Composites containing E-glass fibers and BAG particles are hydrophilic materials that show good wettability characteristics
Adhesion of Respiratory-Infection-Associated Microorganisms on Degradable Thermoplastic Composites
The purpose of this study was to evaluate bacterial adhesion and early colonization on a composite consisting of bioactive glass (BAG) particles and copolymer of ε-caprolactone/D,L-lactide. Materials were incubated with suspensions of both type strains and clinical isolates of Streptococcus pneumoniae, Haemophilus influenzae, and Pseudomonas aeruginosa for 30 minutes (adhesion) and 4 hours (colonization). Clear differences exist in the microorganisms' ability to adhere on the experimental materials. However, the presence of BAG particles does not inhibit bacterial adhesion, but early colonization of the materials with P. aeruginosa was inhibited by the addition of 90–315 μm BAG particles
Organotypic in vitro block culture model to investigate tissue-implant interface. An experimental study on pig mandible
In vitro studies of implant-tissue attachment are primarily based on two-dimensional cell culture models, which fail to replicate the three-dimensional native human oral mucosal tissue completely. Thus, the present study aimed to describe a novel tissue culture model using pig mandibular block including alveolar bone and gingival soft tissues to evaluate the tissue attachment to titanium implant provided with hydrothermally induced TiO2 coating. Tissue attachment on TiO2 coated and non-coated implants were compared. Ti-6Al-4V alloy posts were used to function as implants that were inserted in five pig mandibles. Implants were delivered with two different surface treatments, non-coated (NC) titanium and hydrothermal induced TiO2 coated surfaces (HT). The tissue-implant specimens were cultured at an air/liquid interface for 7 and 14 days. The tissue-implant interface was analyzed by histological and immunohistochemical stainings. The microscopic evaluation suggests that pig tissue explants established soft and hard tissue attachment to both implant surfaces. The epithelial cells appeared to attach to the coated implant. The epithelium adjacent to the implant abutment starts to change its phenotype during the early days of the healing process. New bone formation was seen within small pieces of bone in close contact with the coated implant. In conclusion, this in vitro model maintains the viability of pig tissue and allows histologically and immunohistochemically evaluate the tissue-implant interface. HT-induced TiO2 coating seems to have a favorable tissue response. Moreover, this organotypic tissue culture model is applicable for further studies with quantitative parameters to evaluate adhesion molecules present at the implant-tissue interface.[GRAPHICS]
Effect of bioactive glass air-abrasion on Fusobacterium nucleatum and Porphyromonas gingivalis biofilm formed on moderately rough titanium surface
This aim of this study was to investigate the effects of three types of air-abrasion particles on dual-species biofilms of Fusobacterium nucleatum and Porphyromonas gingivalis, both of which were cultured on sandblasted and acid-etched (SA) titanium discs. Out of 24 SA discs with biofilm, 18 were exposed to either air-abrasion using Bioglass 45S5 (45S5 BG; n = 6), novel zinc (Zn)-containing bioactive glass (Zn4 BG; n = 6), or inert glass (n = 6). The efficiency of biofilm removal was evaluated using scanning electron microscopy (SEM) imaging and culturing techniques. Air-abrasion using 45S5 BG or Zn4 BG demonstrated a significant decrease in the total number of viable bacteria compared to discs air-abraded with inert glass or intact biofilm without abrasion. Moreover, P. gingivalis could not be detected from SEM images nor culture plates after air-abrasion with 45S5 BG or Zn4 BG. The present study showed that air-abrasion with 45S5 or Zn4 bioactive glasses can successfully eradicate dual-biofilm of F. nucleatum and P. gingivalis from sandblasted and acid-etched titanium discs.</p
Gastric acid challenge of lithium disilicate-reinforced glass-ceramics and zirconia-reinforced lithium silicate glass-ceramic after polishing and glazing-impact on surface properties
OBJECTIVES
To investigate the impact of simulated gastric acid on the surface properties of lithium disilicate-reinforced glass-ceramics and zirconia-reinforced lithium silicate glass-ceramic after certain polishing and glazing procedures.
MATERIALS AND METHODS
Four different types of square-shaped specimens (10 × 10 × 2 mm, n = 13) were manufactured: lithium disilicate-reinforced glass-ceramic milled and polished (LDS-P); milled, polished, and glazed (LDS-PG); milled, glazed, and no polishing (LDS-G); and milled and polished zirconia-reinforced lithium silicate glass-ceramic (ZR-LS). Specimens were immersed in hydrochloride acid (HCl 0.06 M, pH 1.2) to simulate gastric acid irritation and stored in the acid for 96 h in 37 °C. Specimen weight, surface gloss, Vickers surface microhardness and surface roughness (R, R, with optical profilometer), and surface roughness on nanometer level (S, S, S/S, S, S with atomic force microscope) were measured before and after the acid immersion.
RESULTS
ZR-LS specimens lost significantly more weight after acid immersion (p = 0.001), also surface microhardness of ZR-LS was significantly reduced (p = 0.001). LDS-G and LDS-PG showed significantly lower surface roughness (S, S) values compared to LDS-P before (p ≤ 0.99) and after (p ≤ 0.99) acid immersion and ZR-LS after acid immersion (p ≤ 0.99).
CONCLUSIONS
Gastric acid challenge affects the surface properties of lithium disilicate-reinforced glass-ceramic and zirconia-reinforced lithium silicate glass-ceramic. Glazing layer provides lower surface roughness, and the glazed surface tends to smoothen after the gastric acid challenge.
CLINICAL RELEVANCE
Surface finish of lithium disilicate-reinforced glass-ceramic and zirconia-reinforced lithium silicate glass-ceramic has a clear impact on material's surface properties. Gastric acidic challenge changes surface properties but glazing seems to function as a protective barrier. Nevertheless, also glazing tends to smoothen after heavy gastric acid challenge. Glazing can be highly recommended to all glass-ceramic restorations but especially in patients with gastroesophageal reflux disease (GERD) and eating disorders like bulimia nervosa
Early Biofilm Formation on UV Light Activated Nanoporous TiO2 Surfaces In Vivo
Purpose. To explore early S. mutans biofilm formation on hydrothermally induced nanoporous TiO2 surfaces in vivo and to examine the effect of UV light activation on the biofilm development. Materials and Methods. Ti-6Al-4V titanium alloy discs (n = 40) were divided into four groups with different surface treatments: noncoated titanium alloy (NC); UV treated noncoated titanium alloy (UVNC); hydrothermally induced TiO2 coating (HT); and UV treated titanium alloy with hydrothermally induced TiO2 coating (UVHT). In vivo plaque formation was studied in 10 healthy, nonsmoking adult volunteers. Titanium discs were randomly distributed among the maxillary first and second molars. UV treatment was administered for 60 min immediately before attaching the discs in subjects' molars. Plaque samples were collected 24h after the attachment of the specimens. Mutans streptococci (MS), non-mutans streptococci, and total facultative bacteria were cultured, and colonies were counted. Results. The plaque samples of NC (NC + UVNC) surfaces showed over 2 times more often S. mutans when compared to TiO2 surfaces (HT + UVHT), with the number of colonized surfaces equal to 7 and 3, respectively. Conclusion. This in vivo study suggested that HT TiO2 surfaces, which we earlier showed to improve blood coagulation and encourage human gingival fibroblast attachment in vitro, do not enhance salivary microbial (mostly mutans streptococci) adhesion and initial biofilm formation when compared with noncoated titanium alloy. UV light treatment provided Ti-6Al-4V surfaces with antibacterial properties and showed a trend towards less biofilm formation when compared with non-UV treated titanium surfaces
Antibacterial properties of bioactive glass particle abraded titanium against Streptococcus mutans
The purpose of this study was to evaluate effects of titanium surfaces air-abraded with particles of Bioglass® 45S5 and three-ZnO and SrO doped compositions on the viability, adhesion and biofilm formation of Streptococcus mutans. A statistically significant decrease in the viability of S. mutans was observed for all titanium discs air-particle abraded with the BAGs (p S. mutans adhesion on titanium surfaces treated with different glasses (p = 0.964). Static SBF immersion experiments showed that after 2 and 48 h the BAG doped with 4 mol% ZnO demonstrated the highest Zn2+ ion concentration released into SBF (0.2 mg L−1). 45S5 BAG demonstrated the highest statistically significant increase in the pH throughout the 120 min of static immersion (p S. mutans and they suppressed S. mutans biofilm formation. The antimicrobial activity of 45S5 BAG was attributed to high pH whereas for the Zn-containing BAGs antimicrobial activity was due to steady release of Zn2+ into the interfacial solution.</p
Effect of bioactive glass air-abrasion on the wettability and osteoblast proliferation on sandblasted and acid-etched titanium surfaces
The aim of this study was to evaluate the hydrophilicity, surface free energy, and proliferation and viability of human osteoblast-like MC3T3-E1 cells on sandblasted and acid-etched titanium surfaces after air-abrasion with 45S5 bioactive glass, zinc-containing bioactive glass, or inert glass. Sandblasted and acid-etched titanium discs were subjected to air-abrasion with 45S5 bioactive glass, experimental bioactive glass (Zn4), or inert glass. Water contact angles and surface free energy were evaluated. The surfaces were studied with preosteoblastic MC3T3-E1 cells. Air-abrasion with either type of glass significantly enhanced the hydrophilicity and surface free energy of the sandblasted and acid-etched titanium discs. The MC3T3-E1 cell number was higher for substrates air-abraded with Zn4 bioactive glass and similar to that observed on borosilicate coverslips (controls). Confocal laser scanning microscopy images showed that MC3T3-E1 cells did not spread as extensively on the sandblasted and acid-etched and bioactive glass-abraded surfaces as they did on control surfaces. However, for 45S5- and Zn4-treated samples, the cells spread most at the 24 h time point and changed their morphology to more spindle-like when cultured further. Air-abrasion with bioactive glass and inert glass was shown to have a significant effect on the wettability and surface free energy of the surfaces under investigation. Osteoblast cell proliferation on sandblasted and acid-etched titanium discs was enhanced by air-abrasion with 45S5 bioactive glass and experimental Zn4 bioactive glass compared with air-abrasion with inert glass or no air-abrasion
Midline denture base strains of glass fiber-reinforced single implant-supported overdentures
Statement of problemThe fracture incidence of implant-supported overdentures is more frequent in the area of attachment because of stress concentration and denture deformation in this area. How E-glass fiber reinforcement can address this problem is unclear.PurposeThe purpose of this in vitro study was to evaluate the influence of unidirectional E-glass fiber reinforcement on the mid-line denture base strains of single implant-supported overdentures.Material and methodsAn experimental acrylic resin cast was constructed with a single implant placed in the mid-line area and a ball attachment screwed to the implant. Twenty-four experimental overdentures were constructed and divided into 4 groups: group AP fabricated from autopolymerizing acrylic resin without fiber reinforcement, group APF fabricated from autopolymerizing acrylic resin with unidirectional E-glass fiber reinforcement running over the residual ridge and the ball matrix, group HP fabricated from heat-polymerized acrylic resin without fiber reinforcement, and group HPF fabricated from heat-polymerized acrylic resin with unidirectional E-glass fiber reinforcement running over the residual ridge and the ball matrix. A biaxial rosette strain gauge was attached to the incisor areas of each overdenture above the attachment level (Ch1, Ch2) and to a multichannel digital strain meter. A static vertical load of 100 N was applied to the first molar area bilaterally by using a universal testing device during strain measurement procedures. The differences in the mean strain and deflection values among the investigated groups were evaluated for statistical significance using 1-way analysis of variance (ANOVA) with the Tukey post hoc multiple comparison (α=.05).ResultsThe type of acrylic resin did not have a statistically significant effect on the mean strain values among groups (P=.350), while the reinforcement did significantly affect them (PConclusionsUnidirectional E-glass fiber reinforcement placed over the residual ridge and implant attachment significantly reduced denture base strains and deformation of single implant-supported overdentures.</p
Biomechanical aspects of reinforced implant over-dentures: a systematic review
AbstractPurposeThe purpose of this systematic review was to investigate the effect of reinforcement on the mechanical behaviour of implant overdenture (IOD) bases and its cumulative biological effect on the underlying supporting structures (implants and the residual ridge).Material and methodsThe required documents were collected electronically from PubMed and Web of Science databases targeting papers published in English that focused on denture base reinforcement for IOD prostheses in order to recognize the principal outcomes of reinforcement on the mechanical and biological properties of overdentures. Such biological outcomes as: strains on implants, peri-implant bone loss, residual ridge resorption, and strain on the residual alveolar ridge.ResultsA total of 269 citations were identified. After excluding any repeated articles between databases and the application of exclusion and inclusion criteria, only 13 publications fulfilled the inclusion criteria. Three publications investigated the mechanical properties of fibre and/or metal-reinforced implant overdentures while another 3 articles investigated the effect of metal reinforcement on stress distribution and strains transmitted to the underlying implants. In addition, 3 in vitro studies investigated the effect of metal reinforcement on overdenture base strain and stresses. Stress distribution to the residual ridge and strain characteristics of the underlying tissues were investigated by 2 in vitro studies. Five clinical studies performed to assist the clinical and prosthetic maintenance of metal-reinforced IOD were included. Data concerning denture base fracture, relining, peri-implant bone loss, probing depth, and implant survival rates during the functional period were extracted and considered in order to evaluate the mechanical properties of the denture base, residual ridge resorption and implant preservation rates, respectively.ConclusionThe use of a denture base reinforcement can reduce the fracture incidence in IOD bases by enhancing their flexural properties and reducing the overdenture base deformation. Strains on the underlying supporting structures of overdenture prostheses including dental implants and the residual ridge can be decreased and evenly distributed using a metal reinforcement.</div