80 research outputs found
In-Situ Nuclear Magnetic Resonance Investigation of Strain, Temperature, and Strain-Rate Variations of Deformation-Induced Vacancy Concentration in Aluminum
Critical strain to serrated flow in solid solution alloys exhibiting dynamic strain aging (DSA) or Portevin–LeChatelier effect is due to the strain-induced vacancy production. Nuclear magnetic resonance (NMR) techniques can be used to monitor in situ the dynamical behavior of point and line defects in materials during deformation, and these techniques are nondestructive and noninvasive. The new CUT-sequence pulse method allowed an accurate evaluation of the strain-enhanced vacancy diffusion and, thus, the excess vacancy concentration during deformation as a function of strain, strain rate, and temperature. Due to skin effect problems in metals at high frequencies, thin foils of Al were used and experimental results correlated with models based on vacancy production through mechanical work (vs thermal jogs), while in situ annealing of excess vacancies is noted at high temperatures. These correlations made it feasible to obtain explicit dependencies of the strain-induced vacancy concentration on test variables such as the strain, strain rate, and temperature. These studies clearly reveal the power and utility of these NMR techniques in the determination of deformation-induced vacancies in situ in a noninvasive fashion.
In situ nuclear magnetic resonance study of defect dynamics during deformation of materials
Nuclear magnetic resonance techniques can be used to monitor in situ the dynamical behaviour of point and line defects in materials during deformation. These techniques are non-destructive and non-invasive. We report here the atomic transport, in particular the enhanced diffusion during deformation by evaluating the spin lattice relaxation time in the rotating frame, T-1p, in pure NaCl single crystals as a function of temperature (from ambient to about 900 K) and strain-rate (to approximate to 1.0s(-1)) in situ during deformation. The strain-induced excess vacancy concentration increased with the strain-rate while in situ annealing of these excess defects is noted at high temperatures. Contributions due to phonons or paramagnetic impurities dominated at lower temperatures in the undeformed material. During deformation, however, the dislocation contribution became predominant at these low temperatures. The dislocation jump distances were noted to decrease with increase in temperature leading to a reduced contribution to the overall spin relaxation as temperature is increased. Similar tests with an improved pulse sequence (CUT-sequence), performed on ultra-pure NaCl and NaF single crystals revealed slightly different results; however, strain-enhanced vacancy concentrations were observed. The applicability of these techniques to metallic systems will be outlined taking thin aluminium foils as an example
Recommended from our members
Corrosion and failure processes in high-level waste tanks
A large amount of radioactive waste has been stored safely at the Savannah River and Hanford sites over the past 46 years. The aim of this report is to review the experimental corrosion studies at Savannah River and Hanford with the intention of identifying the types and rates of corrosion encountered and indicate how these data contribute to tank failure predictions. The compositions of the High-Level Wastes, mild steels used in the construction of the waste tanks and degradation-modes particularly stress corrosion cracking and pitting are discussed. Current concerns at the Hanford Site are highlighted
Temperature Dependence of the Dynamics of Portevin-Le Chatelier Effect in Al-2.5%Mg alloy
Tensile tests were carried out by deforming polycrystalline samples of
Al-2.5%Mg alloy at four different temperatures in an intermediate strain rate
regime of 2x10-4s-1 to 2x10-3s-1. The Portevin-Le Chatelier (PLC) effect was
observed throughout the strain rate and temperature region. The mean cumulative
stress drop magnitude and the mean reloading time exhibit an increasing trend
with temperature which is attributed to the enhanced solute diffusion at higher
temperature. The observed stress-time series data were analyzed using the
nonlinear dynamical methods. From the analyses, we could establish the presence
of deterministic chaos in the PLC effect throughout the temperature regime. The
dynamics goes to higher dimension at a sufficiently high temperature of 425K
but the complexity of the dynamics is not affected by the temperature.Comment: 18 pages, 8 figures; accepted in Met. Mater. Trans.
Displacement cascade evolution in tungsten with pre-existing helium and hydrogen clusters: a molecular dynamics study
- …