Effect of Immobilizing Bacillus megaterium on the Compressive Strength and Water Absorption of Mortar

The world’s growing population and industrialization have led to increased construction activities. This has increased the amount of waste aggregates which can be recycled in construction and cut the cost of infrastructure development. This study, therefore, reports the experimental findings for the effect of immobilizing Bacillus megaterium on the compressive strength and water absorption of laboratory prepared test mortar. Bacterial solution used in this work had a concentration of 1.0 × 107 cells/mL. The impact of recycled mortar impregnated with bacteria was studied after curing the specimens in water, saturated lime water, and 1.5% sulfuric acid. Compressive strength for test specimens cured in the three media was determined at the 2nd, 7th, 28th, and 56th day of curing. SEM analysis was done for mortars cured in acidic media and saturated lime water after curing for 28 days. The test results indicated that curing in water and saturated water improved the compressive strength, while the acidic medium lowered it. Recycled mortar is, therefore, an ideal material for immobilizing Bacillus megaterium before introduction into fresh concrete/mortar. The use of recycled mortar is a good strategy to reduce wastes from construction activities, save on the cost of construction materials, and enhance environmental conservation

Review of the Effect of Grinding Aids and Admixtures on the Performance of Cements

Grinding aids (GAs) are polar chemicals introduced in cement mills in either liquid or powder form to improve on mill grindability efficiency. Studies have shown that some GAs not only help in grinding efficiency but also play vital roles in improving the product particle size distribution, product ability to flow in the mill, grinding energy reduction, and improvement on the separator efficiency. This review investigated the impacts of the GAs on the performance of some properties of cement when used as either mortar and/or concrete. The influence of the GAs incorporation in cement grinding on properties such as workability and setting times of the placed concrete and/or mortar has been covered in this review. The performance of GAs on ordinary portland cement (OPC) and blended cements with other supplementary cementitious materials such as pozzolana, fly ash, and slag has also been discussed. This is in view to tapping the maximum benefits of using GAs in cement production and use. This review work established that GAs have a positive influence on mill performance when properly applied. It further established that blended cements work better when dosed with additives such as GAs and/or quality improvers when compared to OPC. The review work demonstrated that some superplasticizers help in lowering the water demand in highly blended pozzolanic-based cements. The review finally recommended that the future course of action in the production of blended cements should apply GAs. This is in order to help produce highly replaced blended cements that are sustainable

Biocementation Influence on Flexural Strength and Chloride Ingress by Lysinibacillus sphaericus and Bacillus megaterium in Mortar Structures

The concrete/mortar durability performance depends mainly on the environmental conditions, the microstructures, and its chemistry. Cement structures are subject to deterioration by the ingress of aggressive media. This study focused on the effects of Bacillus megaterium and Lysinibacillus sphaericus on flexural strength and chloride ingress in mortar prisms. Microbial solutions with a concentration of 1.0 × 107 cells/ml were mixed with ordinary Portland cement (OPC 42.5 N) to make mortar prisms at a water/cement ratio of 0.5. Four mortar categories were obtained from each bacterium based on mix and curing solution. Mortar prisms of 160 mm × 40 mm × 40 mm were used in this study. Flexural strength across all mortar categories was determined at the 14th, 28th, and 56th day of curing. Mortars prepared and cured using bacterial solution across all curing ages exhibited the highest flexural strength as well as the highest percent flexural strength gain. Lysinibacillus sphaericus mortars across all mortar categories showed higher flexural strength and percent flexural strength gain than Bacillus megaterium mortars. The highest percent flexural strength gain of 33.3% and 37.0% was exhibited by the 28th and 56th day of curing, respectively. The mortars were subjected to laboratory prepared 3.5% by mass of sodium chloride solution under the accelerated ion migration test method for thirty-six hours using a 12 V Direct Current power source after their 28th day of curing. After subjecting the mortar cubes to Cl media, their core powder was analyzed for Cl content. From these results, the apparent diffusion coefficient, Dapp, was approximated from solutions to Fick’s 2nd Law using the error function. Bacillus megaterium mortars across all mortar categories showed lower apparent diffusion coefficient values with the lowest being 2.6456 × 10–10 while the highest value for Lysinibacillus sphaericus mortars was 2.8005 × 10–10. Both of the test bacteria lowered the ordinary Portland cement Cl-ingress but Bacillus megaterium was significantly more effective than Lysinibacillus sphaericus in inhibition

Chloride Ingress in Cement Mortars Exposed to Acidithiobacillus thiooxidans Bacteria

Concrete structures placed in aggressive aqueous environments are vulnerable to degradation. Majority of studies have linked structural failures to the ingress of deleterious ions into the cement matrix. Some microbial activities may accelerate the penetration of harmful materials into the cement matrix and hence cause pronounced deterioration. This work reports a laboratory-simulated study carried out to determine the extent of chloride ingress in cement mortars exposed to Acidithiobacillus thiooxidans. Test prisms were cast from Portland pozzolana cement (PPC) and ordinary Portland cement (OPC) with water-to-cement ratio maintained at 0.5. Acidithiobacillus thiooxidans bacterial solution of concentration 1.0×107 cell/mL was used to prepare microbial mortar prisms, whereas distilled water was used to prepare the control mortar prisms. The test prisms were subjected to porosity and accelerated chloride ingress after 28th day of curing. Compressive strength was determined after the 2nd, 7th, 28th, and 56th days of curing. Apparent diffusion coefficients (Dapp) were estimated from the solutions to Fick’s second law of diffusion. After the 56th day of curing, the microbial-treated mortars exhibited a significant reduction in compressive strength. The resultant percentage decrease in compressive strength was 30.74% and 19.88% for OPC and PPC, respectively. Further, microbial-treated mortars demonstrated both high porosity and chloride ingress as compared to the control test mortars. Scanning electron microscopy (SEM) and X-ray diffraction (XRD) analyses showed the formation of new deleterious products in the microbial-exposed mortars