Upper critical field, lower critical field and critical current density of FeTe0.60Se0.40 single crystal

The transport and magnetic studies are performed on high quality FeTe0.60Se0.40 single crystals to determine the upper critical fields (Hc2), lower critical field (Hc1) and the Critical current density (Jc). The value of upper critical field Hc2 are very large, whereas the activation energy as determined from the slope of the Arrhenius plots are was found to be lower than that in the FeAs122 superconductor. The lower critical field was determined in ab direction and c direction of the crystal, and was found to have a anisotropy of 'gamma'{=(Hc1//c) / (Hc1//b)} ~ 4. The magnetic isotherms measured up to 12 Tesla shows the presence of fishtail behavior. The critical current densities at 1.8K of the single crystal was found to almost same in both ab and c direction as 1X105 Amp/cm2 in low field regime.Comment: 9 pages, 6 figure

High temperature superconductivity (Tc onset at 34K) in the high pressure orthorhombic phase of FeSe

We have studied the structural and superconducting properties of tetragonal FeSe under pressures up to 26GPa using synchrotron radiation and diamond anvil cells. The bulk modulus of the tetragonal phase is 28.5(3)GPa, much smaller than the rest of Fe based superconductors. At 12GPa we observe a phase transition from the tetragonal to an orthorhombic symmetry. The high pressure orthorhombic phase has a higher Tc reaching 34K at 22GPa.Comment: 15 pages, 4 figure