Anaerobic Biodegradation Tests of Poly(lactic acid) under Mesophilic and Thermophilic Conditions Using a New Evaluation System for Methane Fermentation in Anaerobic Sludge

Anaerobic biodegradation tests of poly(lactic acid) (PLA) powder were done at the thermophilic (55 °C) and mesophilic temperature (35 °C) under aquatic conditions [total solid concentrations of the used sludge were 2.07% (at 55 °C) and 2.24% (at 35 °C)] using a newly developed evaluation system. With this system, the evolved biogas is collected in a gas sampling bag at atmospheric pressure. This method is more convenient than using a pressure transducer or inverted graduated cylinder submerged in water. PLA was degraded about 60% in 30 days, about 80% in 40 days and about 90% in 60 days at 55 °C. On the other hand, the PLA degradation started in 55 days at 35 °C and degradation rate was much slower than at 55 °C

Biodegradation of Poly(butylene succinate) Powder in a Controlled Compost at 58 °C Evaluated by Naturally-Occurring Carbon 14 Amounts in Evolved CO2 Based on the ISO 14855-2 Method

The biodegradabilities of poly(butylene succinate) (PBS) powders in a controlled compost at 58 °C have been studied using a Microbial Oxidative Degradation Analyzer (MODA) based on the ISO 14855-2 method, entitled “Determination of the ultimate aerobic biodegradability of plastic materials under controlled composting conditions—Method by analysis of evolved carbon dioxide—Part 2: Gravimetric measurement of carbon dioxide evolved in a laboratory-scale test”. The evolved CO2 was trapped by an additional aqueous Ba(OH)2 solution. The trapped BaCO3 was transformed into graphite via a serial vaporization and reduction reaction using a gas-tight tube and vacuum manifold system. This graphite was analyzed by accelerated mass spectrometry (AMS) to determine the percent modern carbon [pMC (sample)] based on the 14C radiocarbon concentration. By using the theory that pMC (sample) was the sum of the pMC (compost) (109.87%) and pMC (PBS) (0%) as the respective ratio in the determined period, the CO2 (respiration) was calculated from only one reaction vessel. It was found that the biodegradabilities determined by the CO2 amount from PBS in the sample vessel were about 30% lower than those based on the ISO method. These differences between the ISO and AMS methods are caused by the fact that part of the carbons from PBS are changed into metabolites by the microorganisms in the compost, and not changed into CO2

Biodegradability Evaluation of Polymers by ISO 14855-2

Abstract: Biodegradabilities of polymers and their composites in a controlled compost were described. Polycaprolactone (PCL) and poly(lactic acid) (PLA) were employed as biodegradable polymers. Biodegradabilities of PCL and PLA samples in a controlled compost were measured using a Microbial Oxidative Degradation Analyzer (MODA) according to ISO 14855-2. Sample preparation method for biodegradation test according to ISO/DIS 10210 was also described. Effects of sizes and shapes of samples on biodegradability were studied. Reproducibility of biodegradation test of ISO 14855-2 by MODA was confirmed. Validity of sample preparation method for polymer pellets, polymer film, and polymer products of ISO/DIS 10210 for ISO 14855-2 was confirmed

Study of resonance crossing in FFAG

strong candidate for muon accelerators of the neutrino factory because fixed field allows essential fast acceleration for muon. Roughly speaking, we have two schemes to design FFAG optics, scaling and non-scaling [1]. Scaling FFAG has constant betatron tunes, in principle, with the magnetic field having nonlinear components. However, tunes slightly change during acceleration because of imperfection of the field. On the other hand, a condition of constant tunes is given up in non-scaling FFAG to obtain other advantages such as simple lattice composed of only linear elements. Then, beam dynamics of resonance crossing has become an important issue for both scaling and non-scaling FFAG. Since keeping constant tunes is basic strategy to avoid resonance, dynamics of resonance crossing has not been studied sufficiently. There are especially not many experimental studies. We performed beam studies ofthird order resonance crossing at PoP FFAG and HIMAC synchrotron. Their main results are described in this paper

Quick Preparation of Moisture-Saturated Carbon Fiber-Reinforced Plastics and Their Accelerated Ageing Tests Using Heat and Moisture

A quick method involving the control of heat and water vapor pressure for preparing moisture-saturated carbon fiber-reinforced plastics (CFRP, 8 unidirectional prepreg layers, 1.5 mm thickness, epoxy resin) has been developed. The moisture-saturated CFRP sample was obtained at 120 °C and 0.2 MPa water vapor in 72 h by this method using a sterilizer (autoclave). The bending strength and viscoelastic properties measured by a dynamic mechanical analysis (DMA) remained unchanged during repetitive saturation and drying steps. No degradation and molecular structural change occurred. Furthermore an accelerated ageing test with two ageing factors, i.e., heat and moisture was developed and performed at 140–160 °C and 0.36–0.62 MPa water vapor pressure by using a sealed pressure-proof stainless steel vessel (autoclave). The bending strength of the sample decreased from 1107 to 319 MPa at 160 °C and 0.63 MPa water vapor pressure in 9 days. Degraded samples were analyzed by DMA. The degree of degradation for samples was analyzed by DMA. CFRP and degraded CFRP samples were analyzed by using a surface and interfacial cutting analysis system (SAICAS) and an electron probe micro-analyzer (EPMA) equipped in a scanning electron microscope