Synthesis of Superhydrophobic Barium Hexaferrite Coatings with Low Magnetic Hardness

Using the multifunctional material barium hexaferrite as an example, the prospects for treatment at a quasi-equilibrium low temperature in an open atmosphere to form superhydrophobic magnetic coatings with pronounced crystalline and magnetic anisotropy have been demonstrated for the first time. The relationship between plasma treatment conditions, structural-phase composition, morphology, and superhydrophobic properties of (0001) films of barium hexaferrite BaFe12O19 on C-sapphire is studied. X-ray photoelectron spectroscopy (XPS), X-ray diffractometry (XRD), scanning electron microscopy (SEM), atomic force microscopy (AFM), as well as magnetometry and moisture resistance analysis, were used as research methods. During plasma treatment with a mass-average temperature of 8–10 kK, intense evaporation and surface melting were observed, and texturing of the deposit along (0001) is found. When the treatment temperature was reduced to 4–5 kK, the evaporation of the material was minimized and magnetic and crystal anisotropy increased. However, the increase in the size of crystallites was accompanied by the transition of oxygen atoms from lattice nodes to interstitial positions. All samples exhibited low coercive fields below 500 Oe, associated with the frustration of the magnetic subsystem. Features of growth of materials with a wurtzite structure were used to form a superhydrophobic coating of barium hexaferrite. Plasma treatment regimes for obtaining self-cleaning coatings are proposed. The use of magnetically hard barium hexaferrite to radically change the properties of a coating is demonstrated herein as an example

Influence of Plasma Treatment Parameters on the Structural-Phase Composition, Hardness, Moisture-Resistance, and Raman-Enhancement Properties of Nitrogen-Containing Titanium Dioxide

The paper shows, for the first time, the prospects of treatment with a quasi-equilibrium low-temperature nitrogen plasma in an open atmosphere for the formation of super-hard, super-hydrophobic TiN/TiO2 composite coatings with pronounced Raman-enhancement properties. X-ray diffractometry (XRD), scanning electron microscopy (SEM), atomic force microscopy (AFM), and Raman spectroscopy, as well as the analysis of hardness and moisture-resistance properties, are used as analytical research methods. During plasma treatment of titanium films on sapphire with a mass average temperature of 4–6 kK, an X-ray amorphous hydrophilic titanium oxide film with a low nitrogen content is formed. The nitrogen content in titanium oxide films increases with increasing treatment temperature up to 6–7 kK. In this case, an X-ray amorphous hydrophobic film is formed. With a further increase in temperature to 7–10 kK, a TiN/TiO2 composite structure based on polycrystalline rutile is formed with increased hydrophobicity and pronounced Raman enhancement properties due to the effective excitation of surface plasmon polaritons. The presence of the crystalline phase increases the dephasing time, which determines the quality of the resonance and the achievable amplification of the electromagnetic field near the TiN inclusions. All treated films on sapphire have a super-hardness above 25 GPa (Vickers hardness test) due to high grain size, the presence of nitrogen-containing inclusions concentrated along grain boundaries, and compressive stresses