Obvious Temperature Difference Along a Pb Cluster-Decorated Carbon Nanowire

Pb nanoclusters were deposited onto a suspended carbon nanowire (CNW), where in situ temperature variable observation was carried out by a transmission electron microscope. The heating temperature was up to 450 °C. Both the melting and evaporation of the Pb nanoparticles on the CNW were retarded when compared to the particles on the support frame. The obvious temperature difference of up to 10 K along the CNW of less than 1 μm was demonstrated. It was attributed to the irradiating dissipation-dependent on the surface area of the decorating Pb particle by calculation

Effect of Size-Dependent Thermal Instability on Synthesis of Zn2 SiO4-SiOx Core–Shell Nanotube Arrays and Their Cathodoluminescence Properties

Vertically aligned Zn2SiO4-SiOx(x < 2) core–shell nanotube arrays consisting of Zn2SiO4-nanoparticle chains encapsulated into SiOx nanotubes and SiOx-coated Zn2SiO4 coaxial nanotubes were synthesized via one-step thermal annealing process using ZnO nanowire (ZNW) arrays as templates. The appearance of different nanotube morphologies was due to size-dependent thermal instability and specific melting of ZNWs. With an increase in ZNW diameter, the formation mechanism changed from decomposition of “etching” to Rayleigh instability and then to Kirkendall effect, consequently resulting in polycrystalline Zn2SiO4-SiOx coaxial nanotubes, single-crystalline Zn2SiO4-nanoparticle-chain-embedded SiOx nanotubes, and single-crystalline Zn2SiO4-SiOx coaxial nanotubes. The difference in spatially resolved optical properties related to a particular morphology was efficiently documented by means of cathodoluminescence (CL) spectroscopy using a middle-ultraviolet emission at 310 nm from the Zn2SiO4 phase