Comparison of milling and solution approach for production of silk particles

Silk particles were produced by regenerating from silk solution, and using a milling method. In the regenerated silk particle production, two methods which are reported to render submicron silk particles were selected. Their particle sizes and structures were compared with particles of milling method already developed by us. The volume median average particle sizes (d(0.5)) of regenerated particles were much higher than what was reported previously. In contrast, milling method could produce particles with adjustable particle sizes ranging from micron to submicron level. All the milled particles had advantage of at least 15. °C higher thermal decomposition temperature than regenerated particles. They had silk II structure, and the crystallinity reduced as particle fineness increased, but remained higher than regenerated particles of similar sizes. © 2014 Elsevier B.V

Structure and characteristics of milled silk particles

This study examined the structure, thermal property, and ion adsorption of silk particles. The particles were prepared by attritor-bead mill combination, using alkaline (pH10) charge repulsion and surfactant steric repulsion methods. Both methods produced particles with a dominant β-sheet structure, similar to the silk fibre. There was no significant difference in the decomposition temperatures for either the silk fibre or the micro/nano silk particles. An important finding from this study is clear evidence of reduction of amorphous content during the final stage of powdering using the bead mill. As a result, despite reduction in β-sheet crystallites with the progressive milling, the relative β-sheet content actually increased during this process. However, intermolecular forces between the β-sheets reduced significantly and hence the XRD results showed significant reduction in crystallinity in nano silk particles but crystal forming segments remained with β-sheet conformations after milling. The structural change influenced the ion-adsorption property where particle-size reduction resulted in a significant increase in both the rate and volume of HCrO4- adsorption. © 2014 Elsevier B.V