6 research outputs found
Occurrence of Mixed Phase in Bi0.5Sr0.5Mn0.9Cr0.1O3 Bulk Sample: Electron Paramagnetic Resonance and Magnetization Studies
We study the effects of 10% Cr substitution in Mn sites of Bi0.5Sr0.5MnO3 on the antiferromagnetic (AFM) (T-N similar to 110 K) transition using structural, magnetic and electron paramagnetic resonance (EPR) techniques. Field cooled (FC) and zero field cooled (ZFC) magnetization measurements done from 400 K down to 4 K show that the compound is in the paramagnetic (PM) phase till 50 K where it undergoes a transition to a short-range ferromagnetic phase (FM). Electron paramagnetic resonance measurements performed in the temperature range of 300 K to 80 K conform with the magnetization measurements as symmetric signals are observed owing to the paramagnetic phase. Below 80 K, signals become asymmetric. Electron paramagnetic resonance intensity peaks at similar to 110 K, the decreasing intensity below this temperature confirming the presence of antiferromagnetism. We conclude that below 50 K the magnetization and EPR results are consistent with a cluster glass phase of BSMCO, where ferromagnetic clusters coexist with an antiferromagnetic background
Effect of Size Reduction on Magnetic Ordering in Sm1-x Ca (x) MnO3 (x=0.35, 0.65 and 0.92) Manganites: Magnetic and EMR Studies
We have employed the highly sensitive electron magnetic resonance technique complimented by magnetization measurements to study the impact of size reduction on the magnetic ordering in nanosized Sm1-x Ca (x) MnO3 (x = 0.35, 0.65 and 0.92). In the bulk form, x = 0.35 sample shows a charge ordering transition at 235 K followed by a mixed magnetic phase, the sample with x = 0.65 exhibits charge order below 275 K and shows an antiferromagnetic insulator phase below 135 K while that with x = 0.92 has a ferromagnetic-cluster glass ground state. Thus, a comparative study of magnetic ground states of bulk and nanoparticles (diameter similar to 25 nm) enables us to investigate size-induced effects on different types of magnetic ordering. It is seen that in the bulk samples the temperature dependences of the EPR parameters are quite different from each other. This difference diminishes for the nanosamples where all the three samples show qualitatively similar behavior. The magnetization measurements corroborate this conclusion
Comparative study of magnetic ordering in bulk and nanoparticles of Sm0.65Ca0.35MnO3: Magnetization and electron magnetic resonance measurements
To explore the effect of size reduction to nanoscale on the hole doped Sm0.65Ca0.35MnO3 compound, dc magnetic measurements and electron magnetic resonance (EMR) were done on bulk and nanoparticle samples in the temperature range 10 <= T <= 300 K. Magnetization measurement showed that the bulk sample undergoes a charge ordering transition at 240K and shows a mixed magnetic phase at low temperature. However, the nanosample underwent a ferromagnetic transition at 75 K, and the charge ordered state was destabilized on size reduction down to nanoscale. The low-temperature ferromagnetic component is found to be enhanced in nanoparticles as compared to their bulk counterpart. Interestingly around room temperature, bulk particles show higher magnetization where as at low temperature nanoparticles show higher magnetization. Ferromagnetism in the bulk is due to super exchange where as ferromagnetism in nanoparticles is due to uncompensated spins of the surface layer. Temperature variation of EMR parameters correlates well with the results of magnetic measurements. The magnetic behaviour of the nanoparticles is understood in terms of the core shell scenario. (C) 2015 AIP Publishing LLC
Study of coexisting phases in Bi doped La0.67Sr0.33MnO3
We report the remarkable phase separation behavior in La0.67Sr0.33MnO3 doped with Bi3+ ion at La site. The temperature dependent resistivity and magnetization of La0.67-xBixSr0.33MnO3 (x>0) show the presence of phase separation of ferromagnetic metallic and charge ordered antiferromagnetic insulating phases. Markedly, the field dependant magnetization studies of La0.67-xBixSr0.33MnO3 (x=0.3) show the metamagnetic nature of ferromagnetic metallic state implying the competition of coexisting ferromagnetic metallic and charge ordered antiferromagnetic phases. The electron spin resonance and exchange bias studies of La0.67-xBixSr0.33MnO3 (x=0.4 and 0.5) substantiate the coexistence of ferromagnetic clusters in antiferromagnetic matrix. (C) 2016 Elsevier B.V. All rights reserved