Structure and magnetism of multiphase Sm0.080Co0.645Fe0.276 powders

A Sm-poor mixture of Fe-substituted Sm2Co17, having the nominal stoichiometry of Sm0.080Co0.645Fe0.276, was ball-milled to explore the possibility of enhancing its remanence through direct microstructural refinement. With milling, the Sm2(Co0.7Fe0.3)17 compound disassociates to a body-centered-cubic supersaturated SmCoFe solid solution and a residual SmCoFe amorphous phase. Correspondingly, the coercive field values first increase, peaking at 0.83 kOe after 180 min of milling, then decrease with continued milling t