A collagen-hydroxyapatite scaffold allows for binding and co-delivery of recombinant bone morphogenetic proteins and bisphosphonates.

An emerging paradigm in orthopedics is that a bone-healing outcome is the product of the anabolic (bone-forming) and catabolic (bone-resorbing) outcomes. Recently, surgical and tissue engineering strategies have emerged that combine recombinant human bone morphogenetic proteins (rhBMPs) and bisphosphonates (BPs) in order to maximize anabolism and minimize catabolism. Collagen-based scaffolds that are the current surgical standard can bind rhBMPs, but not BPs. We hypothesized that a biomimetic collagen-hydroxyapatite (CHA) scaffold would bind both agents and produce superior in vivo outcomes. Consistent with this concept, in vitro elution studies utilizing rhBMP-2 ELISA assays and scintillation counting of (14)C-radiolabeled zoledronic acid (ZA) confirmed delayed release of both agents from the CHA scaffold. Next, scaffolds were tested for their capacity to form ectopic bone after surgical implantation into the rat hind limb. Using CHA, a significant 6-fold increase in bone volume was seen in rhBMP-2/ZA groups compared to rhBMP-2 alone, confirming the ability of ZA to enhance rhBMP-2 bone formation. CHA scaffolds were found to be capable of generating mineralized tissue in the absence of rhBMP-2. This study has implications for future clinical treatments of critical bone defects. It demonstrates the relative advantages of co-delivering anabolic and anti-catabolic agents using a multicomponent scaffold system

Spatial control of bone formation using a porous polymer scaffold co-delivering anabolic RHBMP-2 and anti-resorptive agents

Current clinical delivery of recombinant human bone morphogenetic proteins (rhBMPs) utilises freeze-dried collagen. Despite effective new bone generation, rhBMP via collagen can be limited by significant complications due to inflammation and uncontrolled bone formation. This study aimed to produce an alternative rhBMP local delivery system to permit more controllable and superior rhBMP-induced bone formation. Cylindrical porous poly(lactic-co-glycolic acid) (PLGA) scaffolds were manufactured by thermally-induced phase separation. Scaffolds were encapsulated with anabolic rhBMP-2 (20 μg) ± anti-resorptive agents: zoledronic acid (5 μg ZA), ZA pre-adsorbed onto hydroxyapatite microparticles, (5 μg ZA/2 % HA) or IkappaB kinase (IKK) inhibitor (10 μg PS-1145). Scaffolds were inserted in a 6-mm critical-sized femoral defect in Wistar rats, and compared against rhBMP-2 via collagen. The regenerate region was examined at 6 weeks by 3D microCT and descriptive histology. MicroCT and histology revealed rhBMP-induced bone was more restricted in the PLGA scaffolds than collagen scaffolds (-92.3 % TV, p < 0.01). The regenerate formed by PLGA + rhBMP-2/ZA/HA showed comparable bone volume to rhBMP-2 via collagen, and bone mineral density was +9.1 % higher (p < 0.01). Local adjunct ZA/HA or PS-1145 significantly enhanced PLGA + rhBMP-induced bone formation by +78.2 % and +52.0 %, respectively (p ≤ 0.01). Mechanistically, MG-63 human osteoblast-like cells showed cellular invasion and proliferation within PLGA scaffolds. In conclusion, PLGA scaffolds enabled superior spatial control of rhBMP-induced bone formation over clinically-used collagen. The PLGA scaffold has the potential to avoid uncontrollable bone formation-related safety issues and to customise bone shape by scaffold design. Moreover, local treatment with anti-resorptive agents incorporated within the scaffold further augmented rhBMP-induced bone formation