Significant enhancement of irreversibility field in clean-limit bulk MgB2

Low resistivity ("clean") MgB2 bulk samples annealed in Mg vapor show an increase in upper critical field Hc2(T) and irreversibility field Hirr(T) by a factor of 2 in both transport and magnetic measurements. The best sample displayed Hirr above 14 T at 4.2 K and 6 T at 20 K. These changes were accompanied by an increase of the 40 K resistivity from 1.0 to 18 microohm-cm and a lowering of the resistivity ratio from 15 to 3, while the critical temperature Tc decreased by only 1-2 K. These results point the way to make prepare MgB2 attractive for magnet applications.Comment: 3 pages, 4 figures, submitted to Applied Physics Letter

Local Measurement of Current Density by Magneto-Optical Current Reconstruction in Normally and Overpressure Processed Bi-2223 Tapes

Magneto-optical current reconstruction has been used for detailed analysis of the local critical current density (Jc) variation in monocore Bi-2223 tapes. We find, even in high quality tapes with bulk transport Jc ~ 40 kA/cm^2 (77K, 0T), that there exist local regions which possess current densities of more than 200 kA/cm^2. Overpressure processing at 148 bar significantly improved Jc to 48 kA/cm^2 by improving the connectivity. For the overpressure-processed sample we find that the current distribution is more uniform and that the maximum local current density at 77 K is increased almost to 300 kA/cm^2.Comment: Presented at Applied Superconductivity Conference, Houston, August 4th -9th, 200

Influence of growth temperature on the vortex pinning properties of pulsed laser deposited YBa(2)Cu(3)O(7-x) thin films

Epitaxial high-temperature superconducting YBa(2)Cu(3)O(7-x) thin films grown on 2 degrees miscut (001) (LaAlO(3))(0.3)-(SrAl(0.5)Ta(0.5)O(3))(0.7) substrates by pulsed laser deposition show significant and systematic changes in flux pinning properties on changing the substrate temperature from 730 to 820 degrees C. The bulk pinning force is highest for the 760 degrees C growth, rising to a maximum of 4.4 GN/m(3) at 77 K, though there are indications that vortex pinning strength is even higher for the 730 degrees C growth once allowance for the current-blocking effects of a-axis oriented grains is made. Cross-sectional transmission electron microscope images show that the density of antiphase boundaries, stacking faults, and edge dislocations increases strongly with decreasing growth temperature, and is highest at 730 degrees C. In spite of the enhanced density of the pinning defects mentioned above, their vortex pinning effect is still much smaller than for insulating nanoparticles of high density and optimum size, where pinning forces can be four to five times higher.open121

Development of high critical current density in multifilamentary round-wire Bi2Sr2CaCu2O8+x by strong overdoping

Bi2Sr2CaCu2O8+x is the only cuprate superconductor that can be made into a round-wire conductor form with a high enough critical current density Jc for applications. Here we show that the Jc(5 T,4.2 K) of such Ag-sheathed filamentary wires can be doubled to more than 1.4x10^5 A/cm^2 by low temperature oxygenation. Careful analysis shows that the improved performance is associated with a 12 K reduction in transition temperature Tc to 80 K and a significant enhancement in intergranular connectivity. In spite of the macroscopically untextured nature of the wire, overdoping is highly effective in producing high Jc values.Comment: 4 figure