The diffusion coefficient of scandium in dilute aluminum-scandium alloys

The diffusion coefficient of Sc in dilute Al-Sc alloys has been determined at 748 K, 823 K, and 898 K (475 °C, 550 °C, and 625 °C, respectively) using semi-infinite diffusion couples. Good agreement was found between the results of the present study and both the higher temperature, direct measurements and lower temperature, indirect measurements of these coefficients reported previously in the literature. The temperature-dependent diffusion coefficient equation derived from the data obtained in the present investigation was found to be D(m2/s)=(2.34±2.16)*10-4(m2/s)exp((-(167±6)(kJ/mol))/RT). Combining these results with data from the literature and fitting all data simultaneously to an Arrhenius relationship yielded the expression D(m2/s)=(2.34±0.84)*10-4(m2/s)exp((-(167±2)(kJ/mol))/RT). In each equation given above, R is 0.0083144 kJ/mol K, T is in Kelvin, and the uncertainties are ±1 standard error

Microstructure and Strengthening Mechanisms in an Ultrafine Grained Al-Mg-Sc Alloy Produced by Powder Metallurgy

Additions of Sc to an Al-Mg matrix were investigated, paying particular attention to the influence of Al3Sc precipitates and other dispersoids, as well as grain size, on mechanical behavior. Prior studies have shown that Sc significantly increases the strength of coarse-grained Al-Mg alloys. Prompted by these findings, we hypothesized that it would be of fundamental and technological interest to study the behavior of Sc additions to an ultrafine-grained (UFG) microstructure (e.g., 100\u27s nm). Accordingly, we investigated the microstructural evolution and mechanical behavior of a cryomilled ultrafine grained Al-5Mg-0.4Sc (wt pct) and compared the results to those of an equivalent fine-grained material (FG) produced by powder metallurgy. Experimental materials were consolidated by hot isostatic pressing (HIP\u27ing) followed by extrusion or dual mode dynamic forging. Under identical processing conditions, UFG materials generate large Al3Sc precipitates with an average diameter of 154 nm and spaced approximately 1 to 3 μm apart, while precipitates in the FG materials have a diameter of 24 nm and are spaced 50 to 200 nm apart. The strengthening mechanisms are calculated for all materials and it is determined that the greatest strengthening contributions for the UFG and FG materials are Mg-O/N dispersion strengthening and precipitate strengthening, respectively