Preparation of Collagen/Hydroxyapatite Composites Using the Alternate Immersion Method and Evaluation of the Cranial Bone-Forming Capability of Composites Complexed with Acidic Gelatin and b-FGF

Bone-substitute materials are essential in dental implantology. We prepared collagen (Col)/hydroxyapatite (Hap)/acidic gelatin (AG)/basic fibroblast growth factor (b-FGF) constructs with enhanced bone-forming capability. The Col/Hap apatite composites were prepared by immersing Col sponges alternately in calcium and phosphate ion solutions five times, for 20 and 60 min, respectively. Then, the sponges were heated to 56 °C for 48 h. Scanning electron microscopy/energy-dispersive X-ray spectroscopy, Fourier-transform infrared spectroscopy, and X-ray diffraction analyses showed that the Col/Hap composites contained poorly crystalline Hap precipitates on the Col matrix. Col/Hap composite granules were infiltrated by AG, freeze-dried, and immersed in b-FGF solution. The wet quaternary constructs were implanted in rat cranial bone defects for 8 weeks, followed by soft X-ray measurements and histological analysis. Animal studies have shown that the constructs moderately increase bone formation in cranial bone defects. We found that an alternate immersion time of 20 min led to the greatest bone formation (p < 0.05). Constructs placed inside defects slightly extend the preexisting bone from the defect edges and lead to the formation of small island-like bones inside the defect, followed by disappearance of the constructs. The combined use of Col, Hap, AG, and b-FGF might bring about novel bone-forming biomaterials

Characterization of Five Collagenous Biomaterials by SEM Observations, TG-DTA, Collagenase Dissolution Tests and Subcutaneous Implantation Tests

Collagenous biomaterials that are clinically applied in dentistry have dermis-type and membrane-type, both of which are materials for promoting bone and soft tissue formation. The properties of materials supplied with different types could affect their biodegradation periods. The purpose of this study was to characterize five of these products by four different methods: scanning electron microscopy (SEM) observation, thermogravimetry-differential thermal analysis (TG-DTA), 0.01 wt% collagenase dissolution test, and subcutaneous implantation test in vivo. SEM micrographs revealed that both dermis and membranous materials were fibrous and porous. The membranous materials had higher specific derivative thermal gravimetry (DTG) peak temperatures in TG-DTA at around 320 °C, longer collagenase dissolution time ranging from about 300 to 500 min, and more longevity in mice exceeding 9 weeks than the dermis materials. There existed a correlation between the peak temperature in TG-DTA and the collagenase dissolution time. It was considered that higher cross-link degree among collagen fibrils of the membrane-type collagenous materials might account for these phenomena. The experimental protocol and numerical results obtained could be helpful for selection and future development of fibrous collagenous biomaterials in clinical use

Bone Regeneration of Critical-Size Calvarial Defects in Rats Using Highly Pressed Nano-Apatite/Collagen Composites

Osteo-conductive bone substitute materials are required in dentistry. In this study, highly pressed nano-hydroxyapatite/collagen (P-nHAP/COL) composites were formed by a hydraulic press. Critical-size bone defects (Φ = 6 mm) were made in the cranial bones of 10-week-old Wistar rats, in which P-nHAP/COL and pressed collagen (P-COL) specimens were implanted. Defect-only samples (DEF) were also prepared. After the rats had been nourished for 3 days, 4 weeks, or 8 weeks, ossification of the cranial defects of the rats was evaluated by micro-computed tomography (micro-CT) (n = 6 each). Animals were sacrificed at 8 weeks, followed by histological examination. On micro-CT, the opacity of the defect significantly increased with time after P-nHAP/COL implantation (between 3 days and 8 weeks, p < 0.05) due to active bone regeneration. In contrast, with P-COL and DEF, the opacity increased only slightly with time after implantation, indicating sluggish bone regeneration. Histological inspections of the defect zone implanted with P-nHAP/COL indicated the adherence of multinucleated giant cells (osteoclasts) to the implant with phagocytosis and fragmentation of P-nHAP/COL, whereas active bone formation occurred nearby. Fluorescent double staining indicated dynamic bone-formation activities. P-nHAP/COL is strongly osteo-conductive and could serve as a useful novel bone substitute material for future dental implant treatments