Effect of aromatic hydrocarbon addition on in situ powder-in-tube processed MgB2 tapes

We fabricated in situ powder-in-tube processed MgB2/Fe tapes using aromatic hydrocarbon of benzene, naphthalene, and thiophene as additives, and investigated the superconducting properties. We found that these aromatic hydrocarbons were very effective for increasing the Jc values. The Jc values of 20mol% benzene-added tapes reached 130A/mm2 at 4.2K and 10T. This value was almost comparable to that of 10mol% SiC-added tapes and about four times higher than that of tapes with no additions. Microstructure analyses suggest that this Jc enhancement is due to both the substitution of carbon for boron in MgB2 and the smaller MgB2 grain size.Comment: 6 pages, 4 figure

Spin Squeezing via One-Axis Twisting with Coherent Light

We propose a new method of spin squeezing of atomic spin, based on the interactions between atoms and off-resonant light which are known as paramagnetic Faraday rotation and fictitious magnetic field of light. Since the projection process, squeezed light, or special interactions among the atoms are not required in this method, it can be widely applied to many systems. The attainable range of the squeezing parameter is S^{-2/5}, where S is the total spin, which is limited by additional fluctuations imposed by coherent light and the spherical nature of the spin distribution.Comment: 4 pages,6 figure

Fabrication of high performance MgB2 wires by an internal Mg diffusion process

We succeeded in the fabrication of high-Jc MgB2/Fe wires applying the internal Mg diffusion (IMD) process with pure Mg core and SiC addition. A pure Mg rod with 2 mm diameter was placed at the center of a Fe tube, and the space between Mg and Fe tube was filled with B powder or the powder mixture of B-(5mol%)SiC. The composite was cold worked into 1.2mm diameter wire and finally heat treated at temperatures above the melting point of Mg(~650oC). During the heat treatment liquid Mg infiltrated into B layer and reacted with B to form MgB2. X-ray diffraction analysis indicated that the major phase in the reacted layer is MgB2. SEM analysis shows that the density of MgB2 layer is higher than that of usual powder-in-tube(PIT) processed wires. The wires with 5mol% SiC addition heat treated at 670oC showed Jc values higher than 105A/cm2 in 8T and 41,000A/cm2 in 10T at 4.2K. These values are much higher than those of usual PIT processed wires even compared to the ones with SiC addition. Higher density of MgB2 layer obtained by the diffusion reaction is the major cause of this excellent Jc values.Comment: 7page, 6figure

High transport critical current density obtained for Powder-In-Tube-processed MgB2 tapes and wires using stainless steel and Cu-Ni tubes

MgB2 tapes and wires were fabricated by the Powder-In-Tube method. Stainless steel and Cu-Ni tubes were used as sheath materials, and no heat treatment was applied. The tapes made of stainless steel showed transport critical current density Jc of about 10,000A/cm2 at 4.2K and 5T. A high Jc of about 300,000A/cm2 was obtained by extrapolating the Jc-B curves to zero field. Multifilamentary(7-core) MgB2 wire was successfully fabricated using Cu-Ni tubes. For both tapes and wires the grain connectivity of MgB2 was as good as a high-pressure sintered bulk sample. However, the Jc of the Cu-Ni sheathed wire was lower than the stainless steel sheathed tape due to the lower packing density of MgB2.Comment: 4 pages, 3 figure

Fictitious Magnetic Resonance by Quasi-Electrostatic Field

We propose a new kind of spin manipulation method using a {\it fictitious} magnetic field generated by a quasi-electrostatic field. The method can be applicable to every atom with electron spins and has distinct advantages of small photon scattering rate and local addressability. By using a $\rm{CO_2}$ laser as a quasi-electrostatic field, we have experimentally demonstrated the proposed method by observing the Rabi-oscillation of the ground state hyperfine spin F=1 of the cold $\rm{^{87}Rb}$ atoms and the Bose-Einstein condensate.Comment: 5 pages, 5 figure