3 research outputs found

    Crystal structure of Li_2B_(12)H_(12): a possible intermediate species in the decomposition of LiBH_4

    Get PDF
    The crystal structure of solvent-free Li_2B_(12)H_(12) has been determined by powder X-ray diffraction and confirmed by a combination of neutron vibrational spectroscopy and first-principles calculations. This compound is a possible intermediate in the dehydrogenation of LiBH_4, and its structural characterization is crucial for understanding the decomposition and regeneration of LiBH_4. Our results reveal that the structure of Li_2B_(12)H_(12) differs from other known alkali-metal (K, Rb, and Cs) derivatives

    LiSc(BH_4)_4 as a Hydrogen Storage Material: Multinuclear High-Resolution Solid-State NMR and First-Principles Density Functional Theory Studies

    Get PDF
    A lithium salt of anionic scandium tetraborohydride complex, LiSc(BH_4)_4, was studied both experimentally and theoretically as a potential hydrogen storage medium. Ball milling mixtures of LiBH_4 and ScCl_3 produced LiCl and a unique crystalline hydride, which has been unequivocally identified via multinuclear solid-state nuclear magnetic resonance (NMR) to be LiSc(BH_4)_4. Under the present reaction conditions, there was no evidence for the formation of binary Sc(BH_4)_3. These observations are in agreement with our first-principles calculations of the relative stabilities of these phases. A tetragonal structure in space group I (#82) is predicted to be the lowest energy state for LiSc(BH_4)_4, which does not correspond to structures obtained to date on the crystalline ternary borohydride phases made by ball milling. Perhaps reaction conditions are resulting in formation of other polymorphs, which should be investigated in future studies via neutron scattering on deuterides. Hydrogen desorption while heating these Li−Sc−B−H materials up to 400 °C yielded only amorphous phases (besides the virtually unchanged LiCl) that were determined by NMR to be primarily ScB_2 and [B_(12)H_(12)]^(−2) anion containing (e.g., Li_2B_(12)H_(12)) along with residual LiBH_4. Reaction of a desorbed LiSc(BH_4)_4 + 4LiCl mixture (from 4LiBH_4/ScCl_3 sample) with hydrogen gas at 70 bar resulted only in an increase in the contents of Li_2B_(12)H_(12) and LiBH_4. Full reversibility to reform the LiSc(BH_4)_4 was not found. Overall, the Li−Sc−B−H system is not a favorable candidate for hydrogen storage applications

    Study of aluminoborane compound AlB_4H_(11) for hydrogen storage

    Get PDF
    Aluminoborane compounds AlB_4H_(11), AlB_5H_(12), and AlB_6H_(13) were reported by Himpsl and Bond in 1981, but they have eluded the attention of the worldwide hydrogen storage research community for more than a quarter of a century. These aluminoborane compounds have very attractive properties for hydrogen storage: high hydrogen capacity (i.e., 13.5, 12.9, and 12.4 wt % H, respectively) and attractive hydrogen desorption temperature (i.e., AlB_4H_(11) decomposes at ~125 °C). We have synthesized AlB_4H_(11) and studied its thermal desorption behavior using temperature-programmed desorption with mass spectrometry, gas volumetric (Sieverts) measurement, infrared (IR) spectroscopy, and solid state nuclear magnetic resonance (NMR). Rehydrogenation of hydrogen-desorbed products was performed and encouraging evidence of at least partial reversibility for hydrogenation at relatively mild conditions is observed. Our chemical analysis indicates that the formula for the compound is closer to AlB_4H_(12) than AlB_4H_(11)
    corecore