Overcritical state in superconducting round wires sheathed by iron

Magnetic measurements carried out on MgB_2 superconducting round wires have shown that the critical current density J_c(B_a) in wires sheathed by iron can be significantly higher than that in the same bare (unsheathed) wires over a wide applied magnetic field B_a range. The magnetic behavior is, however, strongly dependent on the magnetic history of the sheathed wires, as well as on the wire orientation with respect to the direction of the applied field. The behavior observed can be explained by magnetic interaction between the soft magnetic sheath and superconducting core, which can result in a redistribution of supercurrents in the flux filled superconductor. A phenomenological model explaining the observed behavior is proposed.Comment: 9 pages, 7 figure

Properties of superconducting MgB_2 wires: "in-situ" versus "ex-situ" reaction technique

We have fabricated a series of iron-sheathed superconducting wires prepared by the powder-in-tube technique from (MgB_2)_{1-x}:(Mg+2B)_x initial powder mixtures taken with different proportions, so that x varies from 0 to 1. It turned out that "ex-situ" prepared wire (x = 0) has considerable disadvantages compared to all the other wires in which "in-situ" assisted (0 < x < 1) or pure "in-situ" (x = 1) preparation was used due to weaker inter-grain connectivity. As a result, higher critical current densities J_c were measured over the entire range of applied magnetic fields B_a for all the samples with x > 0. Pinning of vortices in MgB_2 wires is shown to be due to grain boundaries. J_c(B_a) behavior is governed by an interplay between the transparency of grain boundaries and the amount of "pinning" grain boundaries. Differences between thermo-magnetic flux-jump instabilities in the samples and a possible threat to practical applications are also discussed.Comment: To be published in Supercond. Sci. Technol. (2003), in pres