Review of Matrix Metalloproteinases’ Effect on the Hybrid Dentin Bond Layer Stability and Chlorhexidine Clinical Use to Prevent Bond Failure

This review describes the relationship between dentin collagen hybrid bond layer degradation and the Matrix Metalloproteinases (MMPs) after their release by acid etch and rinse adhesives and self etching bonding adhesives that can reduce the bond stability over time. MMP-2, MMP-8 and MMP-9 are indicated as the active proteases that breakdown the collagen fibrils in the hybrid bond layer. Phosphoric acid in the acid etch and rinse bonding process and acid primers in the self etch process are implicated in the release of these proteases and their activation by several non-collagen proteins also released from dentin by the etching. MMPs are released in saliva by salivary glands, by cells in the gingival crevices to crevicular fluid and by pulpal odontoblasts cells to the dentinal fluids. These sources may affect the hybrid layer also. Evidence of the bond strength deterioration over time and the ability of Chlorhexidine to prevent bond deterioration by inhibiting MMP action are discussed. Dentin Bonding procedure utilizing Chlorhexidine for different application times and concentrations are being developed. The application of 2% Chlorhexidine to the phosphoric acid etch surface after rinsing off the acid is the only procedure that has been clinically tested for a longer period of time and shown to prevent bond strength degradation so far. The adoption of this procedure is recommended as means of improving bond stability at this time

Effect of 2% Chlorhexidine Digluconate on the Bond Strength to Normal Versus Caries-affected Dentin

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)This study evaluated the effect of 2% chlorhexidine digluconate (CHX) used as a therapeutic primer on the long-term bond strengths of two etch-and-rinse adhesives to normal (ND) and caries-affected (CAD) dentin. Forty extracted human molars with coronal carious lesions, surrounded by normal dentin, were selected for this study. The flat surfaces of two types of dentin (ND and CAD) were prepared with a water-cooled high-speed diamond disc, then acidetched, rinsed and air-dried. In the control groups, the dentin was re-hydrated with distilled water, blot-dried and bonded with a three-step (Scotchbond Multi-Purpose-MP) or two-step (Single Bond 2-SB) etch-and-rinse adhesive. In the experimental groups, the dentin was rehydrated with 2% CHX (60 seconds), blot-dried and bonded with the same adhesives. Resin composite build-ups were made. The specimens were prepared for microtensile bond testing in accordance with the non-trimming technique, then tested either immediately or after six-months storage in artificial saliva. The data were analyzed by ANOVA/Bonferroni tests (alpha=0.05). CHX did not affect the immediate bond strength to ND or CAD (p>0.05). CHX treatment significantly lowered the loss of bond strength after six months as seen in the control bonds for ND (p0.05). The application of NIP on CHX-treated ND or CAD produced bonds that did not change over six months of storage.342157165Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)Academy of Finland [111724]NIDCR [R01 DE014911]Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)CNPq [473164/2007-8, 300615/2007-8]Academy of Finland [111724]NIDCR [R01 DE014911